Experimental Investigation of the Effect of Processing Parameters on the Formation of Electrospun Polyethylene Oxide Nanofibers

LI Qiang,YANG Ying,JIA Zhidong,GUAN Zhicheng

DOI: https://doi.org/10.3969/j.issn.1003-6520.2007.02.045

2007-01-01

Abstract:Electrospinning is a simple and straightforward process by which continuous polymer fibers with diameter ranging from a few nanometers to microns can be produced using an electrostatically driven jet of polymer solution(or polymer melt).In the present contribution,ultrafine fibers were spun from polyethylene oxide(PEO)/water solution using a homemade electrospinning set-up.The effects of the concentration of polymer solution and spinning voltage on the morphology of fibers and distribution of fiber diameters were investigated.A more comprehensive and systematic understanding of process parameters of the electrospinning was obtained.In this experiment fibers with diameter ranging from 100 nm to 1000 nm were obtained.The results showed that both the concentration of polymer solution and spinning voltage were important factors characterizing the morphology of fibers and distribution of fiber diameters.The concentration of polymer solution played an important role in the morphology of the fibers obtained.Lower concentration of polymer solution(0.04 kg/L PEO aqueous solution) tended to facilitate the formation of fibers with beads,and smooth and uniform fibers without beads were obtained at the concentration of 0.05 kg/L PEO aqueous solution and 0.06 kg/L PEO aqueous solution.As other process parameters were fixed,raising the concentration of polymer solution resulted in the increasing of average diameter of fibers.Spinning voltage also had an influence on the average diameter of fibers.Thinner fibers were received on the target with higher voltage applied on the nozzle at a given flow rate.The morphology of fibers electrospun from PEO was observed and analyzed by scanning electron microscopy(SEM).