Abstract:For the fracture problem of structural steel under strong earthquakes, a continuous damage model which comprehensively considers the influence of stress triaxiality and Lode parameter was proposed in this paper. According to the variation law of Mises stress under cyclic loading, this model decomposes the effective cumulative plastic strain into isotropic hardening and kinematic hardening components, assuming a linear proportional relationship between the fatigue damage induced by these two components. The basic mechanical properties and constitutive relationships of five common Chinese structural steels and four corresponding weld metals were investigated. The fracture failure tests for both notched round bar specimens and pure shear specimens subjected to monotonic tensile and ultra-low-cyclic loading were thoroughly examined on these materials. The continuous damage model parameters were calibrated by means of test results and complementary finite element simulations. Experimental and numerical simulation results indicate that Q690 high strength steel exhibits cyclic softening behavior, whereas the other steels show cyclic hardening characteristics. For pure shear specimens, plane strain specimens and shear energy dissipation cover plates, the continuous damage model was adopted to simulate and analyze the damage development and fracture failure process of the specimens. The predictions for crack initiation, crack propagation and fatigue life are consistent with experimental results, lending further credibility to the model. The calibrated continuous damage model of various steels provides an effective means for analyzing the ULCF fracture failure of structural steel under intense earthquakes.

A Continuum Damage Model for Weld Heat Affected Zone under Low Cycle Fatigue Loading

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

A Modified Microstructure-Based Creep Damage Model for Considering Prior Low Cycle Fatigue Damage Effects

Continuum Damage Mechanics and Numerical Applications

Investigation of low cycle fatigue crack propagation behavior of 316H steel at 550°C based on cyclic response and damage accumulation: experiment and modelling

Continuous damage model for structural steels and weld metals under ultra-low-cyclic loading

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Damage Proportion Analysis of the Combined High and Low Cycle Fatigue Based on the Continuum Damage Mechanics

Cohesive zone modelling of low cycle fatigue cracks in cracked and notched specimens

A continuum damage mechanics model for fatigue degradation and failure of short fiber reinforced composites

Numerical investigation on the creep damage induced by void growth in heat affected zone of weldments

A Continuum Damage Model for Multi-Axial Low Cycle Fatigue of Porous Sintered Metals Based on the Critical Plane Concept

Physical description and model validation of welded joint fatigue damage evolution

Experimental and numerical investigations on extremely-low-cycle fatigue fracture behavior of steel welded joints

Continuum damage mechanics modelling incorporating stress triaxiality effect on ductile damage initiation

Enhanced CDM model accounting of stress triaxiality and Lode angle for ductile damage prediction in metal forming