Abstract:The metallurgical notch effect of weldment is critical for the structural integrity assessment and to avoid the premature failure especially at elevated temperature. The local nonhomogeneous microstructure located in heat affected zone (HAZ) and multi-pass weld metal area (WM) is one of the largest contributions for the material weakening of the entire weldment. Although the type IV failure related to the HAZ has been intensively discussed, few researchers focus on the creep damage on the weld metal. In fact, the limited long-term creep tests of welded joints conducted by Tabuchi et al. [4]. has emphasized the necessity of monitoring creep damage not only in the HAZ but also in the weld metal. In this article, the nonhomogeneous microstructure related creep damage of the CrMoV multi-pass weld metal is discussed in detail. Different fracture morphology subjected to different weld properties are compared with each other, including the distribution of creep cavities, the precipitates and the substructures of crept specimens sampled from weld pass metal in the welding direction (WP), the overlap of different weld passes (WPO) and multiple weld passes through the thickness direction (MWP). Further, the microscopic analysis on the heterogeneous creep damage behavior are conducted. It is found that the grain length difference perpendicular to the loading direction is the dominant reason for anisotropic creep damage of multi-pass weld metal. In addition, the mismatched creep properties of subzones in the multi-pass weld metal also affect the damage field distribution.

Numerical investigation on the creep damage induced by void growth in heat affected zone of weldments

Numerical Simulation of Void Growth Induced Creep Rupture in HAZ at Elevated Temperature

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

A 2-D Mesoscopic Model for the Evaluation of Creep Damage Induced by Void Growth in Polycrystalline Metals

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

Creep Crack Growth Modelling of Grade 91 Vessel Weldments Using a Modified Ductility Based Damage Model

A Modified Microstructure-Based Creep Damage Model for Considering Prior Low Cycle Fatigue Damage Effects

Creep-fatigue life estimation of circumferential welds in thermal high energy piping systems

The development of creep damage constitutive equations for high Cr steel

Creep behavior analysis on ruptured welds of heat-resistant steels with two different failure modes

Nonhomogeneous Microstructure Related Creep Damage of the CrMoV Multi-Pass Weld Metal

Assessment of prior fatigue damage and a new approach to predict remanent creep rupture of P92 steel

Creep Fatigue Damage Assessment Of V-Butt Weld Pipe With An Extended Direct Steady Cycle Analysis

Time-Dependent Fracture and Defect Assessment of Welded Structures at High Temperature

A coupled creep damage evolution model and creep life evaluation

Insight into the creep-fatigue interaction and remaining creep damage mechanisms in different micro-regions of 9%Cr steel welded joints

New Model for Creep Damage Analysis and Its Application to Creep Crack Growth Simulations

Effects of HAZ widths on creep crack growth properties of welded joints

Damage modelling: the current state and the latest progress on the development of creep damage constitutive equations for high Cr steels

Analytical Model to Compare and Select Creep Constitutive Equation for Stress Relief Investigation during Heat Treatment in Ferritic Welded Structure