Preparation and field emission properties of carbon nanotubes cold cathode using melting Ag nano-particles as binder

Y QIN,M HU,H LI,Z ZHANG,Q ZOU

DOI: https://doi.org/10.1016/j.apsusc.2006.08.037

IF: 6.7

2007-01-01

Applied Surface Science

Abstract:A new preparation process for carbon nanotubes (CNTs) cold cathode was studied through the replacement of traditional organic or inorganic binder with Ag nano-particles. This method has the advantages of low preparation temperature and fine electrical contact between CNTs paste and substrate. A mixture paste of CNTs, Ag nano-particles and other organic solvents was spreaded on Si substrate. By melting and connecting of Ag nano-particles after sintered 30min at 250°C, a flat CNTs films with good field emission properties was obtained. The measurements reveal that the turn on electric field and the threshold electric field of as-prepared CNTs cathode are 2.1 and 3.9V/μm respectively and the field emission current density is up to 41mA/cm2 at an applied electric field of 4.7V/μm.