Fabrication of Surface Silvered Polyimide/iron Oxide Composite Films with Both Superparamagnetism and Electrical Conductivity

Jiayu Zhan,Zhanpeng Wu,Shengli Qi,Dezhen Wu,Wantai Yang

DOI: https://doi.org/10.1016/j.tsf.2010.10.034

IF: 2.1

2011-01-01

Thin Solid Films

Abstract:Surface silvered polyimide (PI)/Fe2O3 composite films with both superparamagnetic and surface electrically conductive properties have been fabricated by an in situ technique. Iron (III) 2,4-pentanedionate was incorporated into a PI precursor poly(amic acid) solution and thermally decomposed to form iron oxide nanoparticles in the process of thermal imidization, preparing PI/Fe2O3 nanocomposite films. The establishment of a silver layer on the PI/Fe2O3 film surface involved the steps of chemical etching by the alkaline aqueous solution, ion exchange with silver ions and chemical reduction by glucose. The formed Fe2O3 particles of the nano scale endow the film with typical superparamagnetic response. By employing the etching time of only 10min and a reduction time of no more than 15min, the well-established silver layers have formed on the upside surface. The corresponding reflectivity and resistivity reached to the value of 76.15% and 0.7Ω/square respectively.