Abstract:In order to solve the problems (i.e. low infiltration efficiency, cracks, interface separation and poor mechanical properties) in the process of wood-derived C–SiC composites, the thermal modification of fir at low temperatures (300 °C ∼ 350 °C) combined with sol-gel infiltration was used to successfully produce biomorphic ceramics. The prepared materials were comprehensively characterized and exhibited improved interfacial bonding between C and SiC and mechanical properties. The weight gain per unit volume (0.123 g/cm 3 ) of SiO 2 gel in the fir thermally modified at 300 °C is 167.4%, higher than that (0.046 g/cm 3 ) of the unmodified fir. A well-bonded interface was formed between the SiO 2 gel and the pore wall of the fir thermally modified at 300 °C. With the increase of modification temperature from 300 °C to 350 °C, the distance between SiO 2 gel and the pore wall increases, and a gap (1–3 μm) is observed between SiO 2 gel and the pore wall of the fir carbonized at 600 °C. The C–SiC composites sintered at 1400 °C exhibited the highest compressive strength and bending strength of 40.8 ± 5.8 MPa and 11.7 ± 2.1 MPa, respectively, owing to the well-bonded interface between C of fir thermally modified at 300 °C and SiC. However, the composites sintered at 1600 °C for 120 min exhibited the lowest compressive strength and bending strength of 28.1 ± 13.4 MPa and 5.7 ± 1.6 MPa, respectively, which are 31.1% and 51.3% lower than those sintered at 1400 °C for 120 min, respectively. This might result from the porous structure formed by the excessive consumption of fir-derived carbon during the reaction between C and SiO 2 at 1600 °C for 120 min. Therefore, thermal modification in the preparation of biomorphic C–SiC composites can promote slurry infiltration and the formation of a well-bonded interface between C and SiC, thus improving the mechanical properties of the composites.

Improvement of High-Temperature Mechanical Properties of Heat Treated Cf/geopolymer Composites by Sol-SiO2 Impregnation

Effects of high-temperature heat treatment on the mechanical properties of unidirectional carbon fiber reinforced geopolymer composites

Effect of Heat Treatment on Mechanical Properties of Unidirectional Carbon Fiber Reinforced Geopolymer Composites

Effects of high-temperature heat treatment on the microstructure and mechanical performance of hybrid Cf-SiCf-(Al2O3p) reinforced geopolymer composites

Preparation and in-situ high-temperature mechanical properties of Cf-SiCf reinforced geopolymer composites

Effect of High Temperature Heat Treatment on Mechanical Property of Cr-Geopolymer Composite

Preparation of fully stabilized cubic-leucite composite through heat-treating Cs-substituted K-geopolymer composite at high temperatures

Thermal-mechanical Properties of Short Carbon Fiber Reinforced Geopolymer Matrix Composites Subjected to Thermal Load

Preparation and characterization of Cf/Pollucite composites through geopolymer precursors

Preparation and Mechanical Properties of Carbon Fiber Reinforced Geopolymer Composites

Effect of high temperature heating on the microstructure and performance of cesium-based geopolymer reinforced by cordierite

Effects of Fiber Surface Pretreatment and Composite Post-treatment on Mechanical Properties of 2D-Cf /phosphate Geopolymer Matrix Composites

Interface evolution of the Cf/leucite composites derived from Cf/geopolymer composites

Influence of pyrolytic carbon interphase and pyrolysis temperature on the mechanical and tribological properties of Cf/SiC after heat treatment at 1800 °C

Fabrication and high-temperature strength of 2.5D SiO2f /SiO2 composites prepared by a combined vacuum impregnation and sol-gel method

Effect of Curing Temperature on High-Strength Metakaolin-Based Geopolymer Composite (HMGC) with Quartz Powder and Steel Fibers

Low-temperature thermally modified fir-derived biomorphic C–SiC composites prepared by sol-gel infiltration

Effect of High Temperature on the Mechanical Properties of Hierarchical Porous Cenosphere/geopolymer Composite Foams

Mechanical properties and high temperature failure mechanism of carbon fibers reinforced polysilazane-derived SiCN ceramic matrix composites via PIP process

of glass dust and glass fi ber as fl uxing agents for cerami fi able silicone rubber composites

In situ processing of MWCNTs/leucite composites through geopolymer precursor