Preparation of Submicron LaCaMnO Submicron Powder and LaCaMnO–alumina Composites with CMR Effects by a New Method: Precursor Sintering Technique

Hui Liu,Ying Luo,Ming Li

DOI: https://doi.org/10.1016/j.jmatprotec.2007.08.078

IF: 6.3

2008-01-01

Journal of Materials Processing Technology

Abstract:We have successfully synthesized submicron LaCaMnO powder (with a nominal composition of La0.67Ca0.33MnO3) and the LaCaMnO–Al2O3 composite powder by a newly invented precursor sintering technique. It is found that the precursor solution containing polyacrylamide and citric acid can facilitate the formation of LaCaMnO powders at a relatively lower sintering temperature because PAM and citric acid form a polymer network in the solution and the metal ions evenly distribute in the precursor solution. The critical sintering temperature was carefully studied based on X-ray diffraction patterns and scanning electron microscopy images. It turns out that a low-temperature sintering results in nano-sized powders with a particle size of 50–100nm, but a high-temperature sintering leads to larger clusters of 1–3μm. For the LaCaMnO–alumina composites system, secondary phases appear if the sintering temperature is relatively high (1200°C). Magnetoresistance of the LaCaMnO wafer made from the obtained LaCaMnO powder has a maximum of 56.7% at 269K. More appealing is that LaCaMnO–alumina composite powders have a very high MR, 82.5%, even in the same order of the MR of the epitaxial-grown LaCaMnO thin film. Besides, the advantages of the PST method include simple equipment, common chemical compounds and low-cost.