Abstract:Structural systems developed from novel materials that are more durable and less prone to maintenance during the service lifetime are in great demand. Due to many advantages such as being lightweight as well as having high strength, corrosion resistance, and durability, the sandwich composites structures, in particular, have attracted attention as favorable materials for speedy and durable structural constructions. In the present research, an experimental investigation is carried out to investigate the flexural response of sandwich beams with a pre-cracked core-upper facesheet interface located at one end of the beam. During the development of the sandwich beams, an initial pre-cracked debond was created between the core and facesheet by placing a Teflon sheet at the interface. Both three-point and four-point flexural tests were conducted to characterize the flexural behavior of the sandwich beams. The effects of the loading rate, core thickness, and placement of the initial interfacial crack under a compressive or tensile stress state on the response and failure mechanism of Carbon Fiber-Reinforced Polymer (CFRP)/Polyurethane (PU) foam sandwich beams were investigated. It was found that the crack tip of the initial debonding between the upper facesheet and the core served as a damage initiation trigger followed by the fracture failure of the core due to the growth of the initial crack into the core in an out-of-plane mode. Finally, this leads to facesheet damage and rupture under flexural loadings. An increase in the core thickness resulted in a higher peak load, but the failure of the sandwich beam was observed to occur at significantly lower displacement values. It was found that the behavior of sandwich beams with higher core thickness was loading rate-sensitive, resulting in stiffer response as the loading rate was increased from 0.05 to 1.5 mm/s. This change in stiffness (10–15%) could be related to the squeezing of all pore space, resulting in the collapse of cell walls and thereby making the cell behave as a solid material. As a result, the occurrence of the densification phase in thick core beams occurs at a faster rate, which in turn makes the thick cored sandwich beams exhibit loading rate-sensitive behavior.

Responses of Damage and Energy of Sandwich and Multilayer Beams Composed of Metallic Face Sheets and Aluminum Foam Core under Bending Loading

The Failure Behavior of Double-Layer Metal Foam Sandwich Beams under Three-Point Bending

Three-point Bending of Physically Asymmetric Metal Sandwich Beams with Aluminum Foam Core: Failure Behavior and Optimal Design

Analysis of deformation and failure mechanism of sandwich beams with lattice core under three-point bending load

Failure Analysis of Sandwich Beams under Three-Point Bending Based on Theoretical and Numerical Models

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

Static and Low-Velocity Impact Behavior of Sandwich Beams with Closed-Cell Aluminum-Foam Core in Three-Point Bending

The Failure Behavior of Geometrically Asymmetric Metal Foam Core Sandwich Beams under Three-Point Bending

Large Deflections of Multilayer Sandwich Beams with Metal Foam Cores under Transverse Loading

Low-velocity Impact Response of Sandwich Beams with a Metal Foam Core: Experimental and Theoretical Investigations

Failure Behavior of a Sandwich Beam with GLARE Face-Sheets and Aluminum Foam Core under Three-Point Bending

Quasi-static Bending Response and Energy Absorption of a Novel Sandwich Beam with a Reinforced Auxetic Core under the Fixed Boundary at Both Ends

Dynamic Response of Multilayer Curved Aluminum Honeycomb Sandwich Beams under Low-Velocity Impact

Failure Behavior of Sandwich Beams with Glass Fiber-Reinforced Epoxy/aluminum Laminates Face-Sheets and Aluminum Honeycomb Core under Three-Point Bending

The Load-Carrying Capacity of Sandwich Beams in Different Collapse Mechanisms

Mechanical Properties and Damage Failure of Carbon Fiber Reinforced Polymer Composite Sandwich Structure with Square Honeycomb Core Using the Interlocking Method

Low-Velocity Impact Response of Fully Clamped Metal Foam Core Sandwich Beam Incorporating Local Denting Effect

Plastic Analysis of Multilayer Sandwich Beams with Metal Foam Cores

Plastic analysis of metal foam core sandwich beam transversely loaded by a flat punch: Combined local denting and overall deformation

Flexural Response of Degraded Polyurethane Foam Core Sandwich Beam with Initial Crack between Facesheet and Core

A Comparison of Structural Collapse of Fully Clamped and Simply Supported Hybrid Composite Sandwich Beams with Geometrically Asymmetric Face Sheets