Abstract:Composite sandwich beams with a carbon fiber reinforced polymer (CFRP) square honeycomb core were designed and fabricated by using the interlocking method. The dynamic response and failure mechanism of fully-clamped and simply- supported sandwich beams subjected to low-velocity impact were investigated experimentally and the corresponding failure modes of the sandwich beams were obtained. Meanwhile, the damage evolvement process and the failure mechanism were analyzed in detail. Influences of the impact velocity, boundary conditions, the mass distributions of face sheets and the direction of the slots on the failure modes and load-carrying capacity of the sandwich beams were explored. The low-velocity impact experiments of composites specimens with two kinds of boundary conditions were carried out by using the drop-hammer impact test system. Three kinds of initial impact velocity were considered for the simply-supported and the fully- clamped sandwich beams sandwich beams, respectively. In the experiments, the time history curves of the impact load and the midspan deflection of the specimens were recorded by a load cell and a laser displacement sensor. Meanwhile, the deformation processes of the sandwich beams were captured by a high-speed camera. The experimental results show that the directions for the slots of the long ribs have significant influence on the failure modes of the sandwich beams. The sandwich core with the upward slots at the midspan has compression deformation whilst the cracking failure along the direction of the downward slots at the midspan is observed due to the tension, which results in the face-sheet debonding and rib fracture successively. It is found that for the same mass, the design of the thicker upper face sheet can enhance the impact resistance of the sandwich beams. The peak load and load-carrying capacity of the sandwich beams increase with increasing the impact velocity. The fully-clamped boundary conditions make the sandwich beams exhibit hardening post-failure behaviors obviously. After the initial failure at the midspan, the fully-clamped ends of the cores and the face-sheets of the sandwich beams experience the fracture failure.

Static and Low-Velocity Impact Behavior of Sandwich Beams with Closed-Cell Aluminum-Foam Core in Three-Point Bending

Quasi-static and Low-Velocity Impact Behaviors of Steel-Aluminum Foam Sandwich Beams

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

Low-velocity Impact Response of Sandwich Beams with a Metal Foam Core: Experimental and Theoretical Investigations

Three-point Bending of Physically Asymmetric Metal Sandwich Beams with Aluminum Foam Core: Failure Behavior and Optimal Design

Three-point bending of sandwich beams with aluminum foam-filled corrugated cores

Failure Analysis of Sandwich Beams under Three-Point Bending Based on Theoretical and Numerical Models

A Theoretical Study of Low-Velocity Impact of Geometrically Asymmetric Sandwich Beams

The influence of asymmetric faces on low-velocity impact failure of CFRP/aluminum foam composite sandwich beams

Low-velocity Impact Response of Geometrically Asymmetric Slender Sandwich Beams with Metal Foam Core

Dynamic Response of Foam-Filled Sandwich Beam with Circular Shape Core under Low-Velocity Impact

On low-velocity impact response of foam-core sandwich panels

Dynamic Responses of Sandwich Beams with Gradient-Density Aluminum Foam Cores

Dynamic Response of Slender Multilayer Sandwich Beams with Metal Foam Cores Subjected to Low-Velocity Impact

Low-velocity Impact and Minimum Mass Design of Physically Asymmetric Sandwich Beams with Metal Foam Core

Low-velocity impact properties of foam-filled composite lattice sandwich beams: Experimental study and numerical simulation

Low-Velocity Impact Response of Fully Clamped Metal Foam Core Sandwich Beam Incorporating Local Denting Effect

Experimental and theoretical study on the response of the X-frame CFRP sandwich beam under the local impulsive loading

Impact and Damage Prediction of Sandwich Beams with Flexible Core Considering Arbitrary Boundary Effects

Dynamic Response of Foam-Filled X-type Sandwich Beam under Low-Velocity Impact

Low-velocity impact response and failure mechanism of CFRP sandwich beams with a square honeycomb core fabricated by the interlocking method