Abstract:This present article deals with bending deformation and failure behavior of sandwich and multilayer beams composed of aluminum foam core and metallic face sheets analyzed by in-situ surface displacement analysis (SDA). The effect of beam structure on the failure mode of beam and the energy absorbed by beam failure were investigated and discussed. The SDA results revealed that collapse of the sandwich beams is by two basic modes, indentation (ID) and core shear (CS). The ID is localized deformation on the beam adjacent to the inner or outer roller in four-point bending, where displacement and compressive strains are at the maximum. As for CS mode, failure occurs in the core between inner and outer rollers, which corresponds to the maximum shear strain; discontinuous displacements in both the vertical and horizontal directions are the primary factors for shear crack initiation, growth, and broadening. The failure of the multilayer beams depends on whether the face sheets show ID mode or otherwise. If a single layer core sandwich fails in ID mode, the multilayer beams with similar face sheets show mixed ID + CS modes. If a single layer core sandwich fails fully in CS mode, no ID characteristic appears in the similar face sheet multilayer beams. The deformation energy of the beams relates strongly to the structure and geometry of beam. The predication of the bending fracture work W x of a beam is given by W_x /W_5 = 0.3875C + 0.9383 where W 5 is the deformation energy of the beam with a 5-mm core, and C is the thickness ratio of the core x to 5 mm.

The Failure Behavior of Double-Layer Metal Foam Sandwich Beams under Three-Point Bending

The Failure Behavior of Geometrically Asymmetric Metal Foam Core Sandwich Beams under Three-Point Bending

Three-point Bending of Physically Asymmetric Metal Sandwich Beams with Aluminum Foam Core: Failure Behavior and Optimal Design

Failure Analysis of Sandwich Beams under Three-Point Bending Based on Theoretical and Numerical Models

Responses of Damage and Energy of Sandwich and Multilayer Beams Composed of Metallic Face Sheets and Aluminum Foam Core under Bending Loading

The Initial Plastic Failure of Fully Clamped Geometrical Asymmetric Metal Foam Core Sandwich Beams

Failure Mode of Aluminum Foam-Filled Corrugated Sandwich Beam Under Three-Point Bending Load

Three-point bending of sandwich beams with aluminum foam-filled corrugated cores

Failure Behavior of a Sandwich Beam with GLARE Face-Sheets and Aluminum Foam Core under Three-Point Bending

Large Deflections of Multilayer Sandwich Beams with Metal Foam Cores under Transverse Loading

Analysis of deformation and failure mechanism of sandwich beams with lattice core under three-point bending load

Deformation and Failure Mechanisms of Sandwich Beams under Three-Point Bending at Elevated Temperatures

Static and Low-Velocity Impact Behavior of Sandwich Beams with Closed-Cell Aluminum-Foam Core in Three-Point Bending

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

Low-velocity Impact Response of Sandwich Beams with a Metal Foam Core: Experimental and Theoretical Investigations

Plastic Analysis of Multilayer Sandwich Beams with Metal Foam Cores

Failure Behavior of Sandwich Beams with Glass Fiber-Reinforced Epoxy/aluminum Laminates Face-Sheets and Aluminum Honeycomb Core under Three-Point Bending

Indentation of sandwich beams with metal foam core

Indentation of Metal Foam Core Sandwich Beams: Experimental and Theoretical Investigations

Bending Performance of Carbon Fiber–reinforced Polymers/aluminum Sandwich Structure with Different Forming Process and Analysis of Failure Mode

An Analytical Solution for the Large Deflections of a Slender Sandwich Beam with a Metallic Foam Core under Transverse Loading by a Flat Punch