Abstract:Combined experimental and simulation analysis of bending failure of GLARE laminates. GLARE laminate experiences multiple damage modes during bending failure, including fiber fracture, matrix cracking, interlayer delamination, and fracture of aluminum alloy. In most cases, two or more failure modes occur together, which makes the damage process complex and unpredictable. This paper proposes a combination of experimental testing and numerical simulation to investigate the influence of fiber lay‐up direction and center open‐hole on the bending failure behavior of GLARE laminate. Simultaneously, Acoustic Emission (AE) technology was used to monitor the bending process of GLARE laminates in real‐time, and a numerical simulation model for the three‐point bending of GLARE laminates was established. The experimental results showed that the bending strength of intact specimens decreased significantly with the increase of the fiber off‐axis angle, whereas the strength retention of open‐hole specimens increased significantly with the increase of the fiber off‐axis angle. Based on the K‐means++ clustering algorithm, the peak frequencies corresponding to different damage modes of GLARE laminates were identified as follows: aluminum alloy damage [1–70 kHz], matrix cracking [93–210 kHz], interlaminar delamination [211–304 kHz], and fiber breakage [304–516 kHz]. The simulation results agreed well with the experimental results, showing that the damage in intact specimens initiated at the laminate edges and propagated sequentially along the thickness direction, while the damage in open‐hole specimens initiated at the hole edges and then propagated towards the laminate edges. Highlights The present study investigated the effects of fiber lay‐up direction and central open‐hole on the bending performance and failure behavior of GLARE laminate. In‐situ monitoring of the GLARE laminate during three‐point bending was conducted using AE technology. A model for simulating the progressive damage of GLARE laminate was established and its accuracy was verified.

Failure Behavior of a Sandwich Beam with GLARE Face-Sheets and Aluminum Foam Core under Three-Point Bending

Failure Behavior of Sandwich Beams with Glass Fiber-Reinforced Epoxy/aluminum Laminates Face-Sheets and Aluminum Honeycomb Core under Three-Point Bending

The Failure Behavior of Geometrically Asymmetric Metal Foam Core Sandwich Beams under Three-Point Bending

Three-point Bending of Physically Asymmetric Metal Sandwich Beams with Aluminum Foam Core: Failure Behavior and Optimal Design

Failure Analysis of Sandwich Beams under Three-Point Bending Based on Theoretical and Numerical Models

Short beam shear damage analysis of GLARE laminates based on digital image correlation and finite element analysis

The Failure Behavior of Double-Layer Metal Foam Sandwich Beams under Three-Point Bending

Static and Low-Velocity Impact Behavior of Sandwich Beams with Closed-Cell Aluminum-Foam Core in Three-Point Bending

Responses of Damage and Energy of Sandwich and Multilayer Beams Composed of Metallic Face Sheets and Aluminum Foam Core under Bending Loading

The influence of asymmetric faces on low-velocity impact failure of CFRP/aluminum foam composite sandwich beams

Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM

Flexural Performance of Sandwich Beams with Lattice Ribs and a Functionally Multilayered Foam Core

Soft impact of GLARE fiber metal laminates

The Initial Plastic Failure of Fully Clamped Geometrical Asymmetric Metal Foam Core Sandwich Beams

Deformation and Failure Mechanisms of Sandwich Beams under Three-Point Bending at Elevated Temperatures

Analysis of deformation and failure mechanism of sandwich beams with lattice core under three-point bending load

Dynamic Response of Sandwich Plates with GLARE Face-Sheets and Honeycomb Core under Metal Foam Projectile Impact: Experimental and Numerical Investigations

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact

A Comparison of Structural Collapse of Fully Clamped and Simply Supported Hybrid Composite Sandwich Beams with Geometrically Asymmetric Face Sheets

Transverse Bending and Axial Compressing Mechanical Characteristics of Carbon Fiber Reinforced Plastic Sandwich Laminated Square Tubes

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading