Influence Mechanism of the Quasicrystalline Phase Content on the Corrosion Resistance of AlCuFe-based Coatings
Wei Li,Yuxin Zhang,Ang Yu,Guo Jin,Hao Wang
DOI: https://doi.org/10.11933/j.issn.1007-9289.20230315002
2023-01-01
China surface engineering
Abstract:Considering the development of China's strategic goal of "ocean power", aluminum alloy components, such as the deck and keel used on the ship surface, face the risk of corrosion failure during long-term service. Currently, the method of preparing a film or coating on the surface of aluminum alloys is typically used to isolate the corrosive medium and effectively protect the matrix material. Among these, thermal spraying technology is widely used for the preparation of anti-corrosion coatings on the surface of aluminum alloys owing to its simple operation and because it is not limited by the size of the parts. Aluminum reference crystal materials have a high strength and hardness owing to their unique structure and excellent properties such as a low friction and corrosion resistance. Thus, they have high potential as protective coating materials on the surface of a new generation of aluminum alloys; however, the poor bonding strength and corrosion resistance in the preparation of quasicrystalline (QC) coatings limit their application. Therefore, in this study, AlCuFe and AlCuFeSc QC coatings are prepared on aluminum alloy substrates using explosive spraying technology based on the long-term service conditions of aluminum alloy parts in a marine environment to improve the corrosion resistance of aluminum alloys and increase their service life. First, the microstructures and phase structures of the powder and coating are characterized using scanning electron microscopy and X-ray diffraction. Subsequently, the binding force and corrosion resistance of the coating are analyzed using a tensile testing machine and electrochemical workstation, and the influence of the QC phase content and corrosion resistance of the coating are studied. The tests reveal that the powder and coating are composed of a I-Al65Cu20Fe15 QC phase and small amount of the beta-AlFe phase. The AlCuFe and AlCuFeSc coatings prepared by explosive spraying have a high density and demonstrate good bonding with the substrate; the bonding strengths of the coatings are determined to be 51.9 MPa and 51.2 MPa, respectively. After annealing at 700 celcius, the content of the coating QC phase increases from 49%, 38% to 93.2%, 92.5%, respectively. In addition, the corrosion resistance of the QC coating before annealing is similar to that of the substrate, and the self-corrosion current density of the annealed QC coating is only one-fifth of that of the aluminum alloy substrate. A further comparison of the surface morphologies of the coatings with different QC contents reveales that as the QC content increases, the flatness of the coating surface increases and the pore distribution decreases, which can effectively prevent the entry of corrosive media. This suggests that an increase in the QC content enhances the corrosion resistance of the coating. The salt-water static hanging test simultaneously demonstrates that no apparent corrosion area formes on the annealed coating surface after 336 h, and the aluminum oxide passivating layer that forms on the surface provides a good protection for the substrate as the content of the QC phase increases. The stability of the QC phase I improves by the introduction of the Sc element into the Al-Cu-Fe icosahedron. This study provides a new idea for the corrosion protection of aluminum alloy surfaces used in ships and a basis for the preparation and application of aluminum reference crystal coatings.