Abstract:The electrochemical co-deposition of Cr-Co oxide coatings at room temperature on 304 stainless steel (SS) was studied using an electrolyte composed of a mixture of ethylene glycol (EG), hydrated metal chloride salts (MCln∙YH2O), and water as a secondary hydrogen donor (HBD). Metallic Cu and Ni undercoats were applied to improve the adhesion of a posterior Cr-Co metallic and oxide layer. The electroactive events that took place during both electrodeposition processes were studied using cyclic voltammetry (CV) and chronoamperometry. The microstructure and composition of the surface layers were studied using scanning electron microscopy (SEM/EDS), X-ray diffraction (XRD) and cross-sectional elemental mapping via transmission electron microscopy (TEM). The surface of steel with the Cr-Co:EG-H2O coating showed greater resistance to pitting corrosion (123.93 mV) compared to untreated stainless steel (62.3 mV). This sample showed a large hystere-sis area, which is associated with high resistance to pitting corrosion by the occurrence of a re-passivation of the sample at a Erep value of 24.31 mV. After the cyclic potentiodynamic polariza-tion (CPP) test, the lowest specific mass loss (0.001 mg/cm2) was achieved for the AISI 304 SS sample coated using EG-water solvents (Cr-Co:EG-H2O), while the untreated AISI 304 SS reached a higher specific mass loss (0.01 mg/cm2). The Electrochemical Impedance Spectroscopy (EIS) tests showed that the uniform corrosion resistance varied significantly from the untreated AISI 304 SS (35 kΩ) to the coated sample (57 kΩ), which is attributed to the protection provided by the chromium and cobalt oxides coating. The best corrosion resistance achieved was correlated with a superhydrophobic character (with a contact angle of 158.41°) of the Cr-Co coatings. This was in turn a consequence of a needle-like morphology characteristic of these oxides.

Microstructure and corrosion behavior of Cr and Cr–P alloy coatings electrodeposited from a Cr(III) deep eutectic solvent

EIS Investigation of the Deposition of Trivalent Chromium Coatings on Al 6063 Alloy

Preparation of Al-Cr-Fe Coatings by Heat Treatment of Electrodeposited Cr/Al Composite Coatings

Microstructure and Corrosion Properties of Electrodeposited CoCrFeMnNi High Entropy Alloy Coatings

The Electrodeposition of Ni-Fe-Cr Alloy Coatings on Mild Steel Surfaces and Evaluation of Corrosion Resistance

Electrodeposition of High-Quality Cr Coatings with Solid Solution Al from Cr2+ Electrolyte

The effects of main salt concentrations and deposition voltages on the structures and properties of cathode plasma electrolytic deposited Cr2O3 coatings

Microstructure and Corrosion Properties of Crmnfeconi High Entropy Alloy Coating

The role of electrolyte ratio in electrodeposition of nanoscale Fe Cr alloy from choline chloride-ethylene glycol ionic liquid: A suitable layer for corrosion resistance

Cr-Co Oxide Coatings Resistant to Corrosion, Electrodeposited on 304 SS Using an Ethylene Glycol-Water Solvent

Microstructure and flow accelerated corrosion resistance of Cr coatings electrodeposited in a trivalent chromium bath

Microstructure Characteristics and Formation Mechanism of Co-Deposition Coating on Plain 45# Carbon Steel via Simultaneous Chro-mising and Nitriding by Pack Cementation Process

Structural and electrochemical corrosion properties of plasma-sprayed CoCrFeNiMo HEA coating in corrosive solutions

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Electrodeposition and corrosion behaviour of nanocrystalline Fe–P coatings

Synergistic Effect of Mo, W, Mn and Cr on the Passivation Behavior of a Fe-Based Amorphous Alloy Coating

Preparation of Crystalline Chromium Coating on Cu Substrate Directly by DC Electrodepositing from Wholly Environmentally Acceptable Cr(III) Electrolyte

Under-deposit Corrosion of Cr-coated Ni-based Alloys in Supercritical Water Oxidation Environment at 500 °C

Structure, Composition and Corrosion Resistance of Zn-Ni-P Alloys Electrodeposited from an Ionic Liquid Based on Choline Chloride

Fundamental understanding on the microstructure and corrosion resistance of Cr-(Cr, Al)2O3 composite coatings in-situ synthetized by reactive plasma spraying

Exploration of electrodeposited process of Ni-Co-Cr coating and investigation of Cr doping strengthening mechanism by indentation simulation