Abstract:Mg-Gd alloys show good mechanical properties due to the strengthening β′ phases. However, the β′ phases are unstable and easily transform into other phases, which leads to the severe performance deterioration at elevated temperatures. In this paper, the tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states were investigated at temperatures from 225 °C to 300 °C under stresses from 50 MPa to 80 MPa. The results showed that the creep behaviors of the solution treated (T4) and peak-aged (T6) alloys were dependent on the critical transition temperature. Microstructure evolution analysis revealed that the creep resistance of the T6 alloy was better than that of the T4 alloy below the critical transition temperature due to the existence of more β′ phases. With further increasing the creep temperature, the formation of β 1 phase and the widening of precipitate-free zones (PFZs) in the T6 alloy significantly deteriorated the creep resistance, while the precipitated β′ phases strengthened the T4 alloy effectively. It resulted in that the T4 alloy exhibited better creep resistance above the critical transition temperature. The stress exponents (3.7–6.2) and creep activation energy (127 kJ mol −1 ) of T4 alloy indicated that the dominated creep mechanism was dislocation climb assisted by lattice self-diffusion of Mg atoms. The stress exponents (3.6–6.4) of T6 alloy were close to that of T4 alloy, while the creep activation energy changed from 94 kJ mol −1 to 192 kJ mol −1 with increasing creep temperature. Observation of dislocation configuration revealed that the creep mechanism of T6 alloy transformed into dislocation cross slip above the critical transition temperature.

Compressive Creep Behaviour of Mg–Li–Al Alloy

Compressive Creep Resistance of Mg–14Li–Al–MgO/Mg2Si Composites

Compressive creep behavior of extruded Mg-4Sm-2Yb-0.6Zn-0.4Zr alloy

Tensile and Compressive Creep Behavior of Coarse-Grained Mg-Al-Sr Castings

Investigation on the asymmetric creep ageing behaviour of 2195-T84 Al-Li alloy under different tensile and compressive stress levels

Compressive creep aging behavior and microstructure evolution in extruded Al-Mg-Si alloy under different temperature and stress levels

Compression creep behaviour of Al-8.5Fe-1.3V-1.7Si alloy

Influence of temperature on creep behavior, mechanical properties and microstructural evolution of an Al-Cu-Li alloy during creep age forming

Creep Behaviors and Microstructure Evolution of Mg-5Y-2Nd-3Sm-0.5Zr Alloys

Microstructure Evolution and Creep Behavior of High-Pressure Die-Cast Mg–9Al–1Zn–1Sr Alloy

High-Temperature Creep Behavior of Mg-9Gd-2Nd-1Ca-0.5Zr Alloy

Creep Aging Properties Variation and Microstructure Evolution for 2195 Al–Li Alloys with Various Loading Rates

Compressive creep behavior of selective electron beam melted high Nb containing TiAl alloy

Tensile Creep Behavior and Microstructure Evolution of Mg-11Gd-2Y-0.5Zr Alloy

Tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states

High Temperature Creep Behavior of Mg-5Y-3Sm-0.8Ca-0.5Sb Alloy

High Temperature Creep Behavior of Mg-6Al-1Zn-1.8Gd-0.9Y Alloy

Creep behavior and mechanical properties of Al-Li-S4 alloy at different aging temperatures

Microstructural evolution of Mg–14Gd–0.4Zr alloy during compressive creep

Mechanical Properties and Creep Behavior of Mg–Al–Ca Alloys

Investigating The Stress Level Impact On The Creep Rupture Behaviour Of 2195-T84 Al-Li Alloy: Experimental And Constitutive Modelling