Abstract:Mg-Gd alloys show good mechanical properties due to the strengthening β′ phases. However, the β′ phases are unstable and easily transform into other phases, which leads to the severe performance deterioration at elevated temperatures. In this paper, the tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states were investigated at temperatures from 225 °C to 300 °C under stresses from 50 MPa to 80 MPa. The results showed that the creep behaviors of the solution treated (T4) and peak-aged (T6) alloys were dependent on the critical transition temperature. Microstructure evolution analysis revealed that the creep resistance of the T6 alloy was better than that of the T4 alloy below the critical transition temperature due to the existence of more β′ phases. With further increasing the creep temperature, the formation of β 1 phase and the widening of precipitate-free zones (PFZs) in the T6 alloy significantly deteriorated the creep resistance, while the precipitated β′ phases strengthened the T4 alloy effectively. It resulted in that the T4 alloy exhibited better creep resistance above the critical transition temperature. The stress exponents (3.7–6.2) and creep activation energy (127 kJ mol −1 ) of T4 alloy indicated that the dominated creep mechanism was dislocation climb assisted by lattice self-diffusion of Mg atoms. The stress exponents (3.6–6.4) of T6 alloy were close to that of T4 alloy, while the creep activation energy changed from 94 kJ mol −1 to 192 kJ mol −1 with increasing creep temperature. Observation of dislocation configuration revealed that the creep mechanism of T6 alloy transformed into dislocation cross slip above the critical transition temperature.

High Temperature Creep Behavior of Mg-5Y-3Sm-0.8Ca-0.5Sb Alloy

High Temperature Creep Behavior of Mg-12Gd-2Y-2Sm-0.5Zr Magnesium Alloy

High Temperature Creep Behavior of Mg-6Al-1Zn-1.8Gd-0.9Y Alloy

Creep Behaviors and Microstructure Evolution of Mg-5Y-2Nd-3Sm-0.5Zr Alloys

High-Temperature Creep Behavior of Mg-9Gd-2Nd-1Ca-0.5Zr Alloy

High Temperature Creep Behavior of Mg-12Gd-2Y-0.5Zr Magnesium Alloy

Creep Behavior and Creep Mechanism of Mg-Gd-Y-Sm-Zr Alloy

Creep Behavior of Ageing Hardened Mg-10Gd-3Y Alloy

The Elevated-Temperature Mechanical Behavior of Peak-Aged Mg–10Gd–3Y–0.4Zr Alloy

Compressive creep behavior of extruded Mg-4Sm-2Yb-0.6Zn-0.4Zr alloy

Tensile Creep Behavior and Microstructure Evolution of Mg-11Gd-2Y-0.5Zr Alloy

High Temperature Creep Behavior of an As-Cast Near-Α Ti–6Al–4Sn–4Zr-0.8Mo–1Nb–1W-0.25Si Alloy

Tensile creep behaviors of Mg-10Gd-0.4Zr alloy in different heat treatment states

Understanding solid solution strengthening at elevated temperatures in a creep-resistant Mg–Gd–Ca alloy

Creep Properties of Mg-12Gd-3Y-1Sm-0.5Zr Alloy

Mechanical Properties and Creep Behavior of Mg-Gd-Y-Zr Alloys

Heat treatment Optimizing and property of Mg-13Gd-3Y-0.4Zr alloy

Effects of heat treatments on tensile properties and creep behavior of Mg-Y-Gd-Zr alloys

Creep Behavior and Precipitation Evolution of Mg-13Gd-2y-0.5zr Alloy

Superior high temperature creep resistance of a cast Al–Mg–Ca-Sc alloy with multi-scale hierarchical microstructures

Room temperature tensile creep behavior of Mg-6Zn-0.4Mn-0.3Al-0.2Ca (wt.%) alloy containing icosahedral quasicrystals