Microstructure and Creep Behavior at High Temperature of In-situ Mg2Si/Mg Composite

CAI Tianxiang,ZHENG Xiaoping,LI Wenfang,DU Jun

2012-01-01

Abstract:The Mg2Si/Mg composite,which contains the various content of Mg2Si,was prepared by in-situ technology.The morphology of the primary Mg2Si was observed by optical microscope,and the creep behaviors of the prepared composite under different temperature and stress were analyzed.The results show that the morphology of the primary Mg2Si changes from block shape to dendritic or petaliform shape with the increase of Mg2Si,and the Mg2Si phases distribute around the α-Mg and the Chinese eutectic Mg2Si.The creep resistance of the composites increases obviously with the increase of Mg2Si.According to the creep power exponent equation,the creep apparent stress exponent and the creep apparent activation energy can be calculated.It is founded that both of them get larger with the increase of the Mg2Si content.Moreover,the creep apparent stress exponents are all over 5,while the creep apparent activation energy is higher than the pure Mg (134 kJ/mol).The creep mechanism of in-situ Mg2Si/Mg composite is probably deem as the dislocation climbing and the second phase strengthing.