Defect Spinel Li8n/N+4mn8/N+4o4 Cathode Materials For Solid-State Lithium-Polymer Batteries

K Tatsumi

DOI: https://doi.org/10.1149/1.1344525

IF: 3.9

2001-01-01

Journal of The Electrochemical Society

Abstract:We have used a self-reaction process, called the JMC (Japanese Metal and Chemical Co., Ltd.) method, to prepare a series of defect spinels Li8n/n+4Mn8/n+4O4, Li4Mn5O12-delta (n = 0 8), Li2Mn3O7-delta (n = 0.65), and Li2Mn4O9-delta (n = 0.5). We found that it is easy to oxidize a defect spinel with a higher lithium content (Li/Mn ratio of 0.8) during synthesis. At the same time, however, the defect spinel easily becomes oxygen deficient. By contrast, a defect spinel with a smaller lithium content, especially Li/Mn of 0.5, is difficult to fully oxidize. The defect spinels deliver at initial capacity of 160 mAh/g both in the liquid-electrolyte and solid-state polymer-electroyte-based cells. Li2Mn3O7-delta shows the best battery performance; the capacity loss rare is 0.18% per cycle for a lithium-polymer cell during the first 100 cycles at 65 degreesC, and the cell gives a specific energy of 360 Wh/kg based on the pure oxide. All compounds are thermally stable up to 200 degreesC when they are in contact with polymer electrolytes; but undergo thermal runaway over 200 degreesC. The exothermic reaction proceeds via a redox reaction among Mn4+, Mn3+, and the polymer electrolyte. (C) 2000 The Electrochemical Society. S0013-4651(00)06-043-2. All rights reserved.