Abstract:Traditional butyl rubber halogenation technology involves the halogenation of IIR using molecular chlorine or bromine in a solution. However, this method is technologically complex. This study investigated a novel method for the halogenation of butyl rubber to enhance its stability and resistance to thermal oxidation and aggressive media. The butyl rubber was modified through mechanochemical modification, induced by solvent swelling in a polychlorinated n-alkane solution. During the modification, samples were obtained with chlorine content ranging from 3 to 15%. After extraction, the halogen content was quantitatively determined with the oxygen flask combustion method and X-ray photoelectron spectroscopy. It was shown that for samples with total chlorine content of up to 6%, there was almost no leaching of chlorine from the samples. The chemical structure of the extracted rubbers was ascertained using FT-IR and 1H NMR spectroscopy, and it was demonstrated that all samples showed absorption peaks and signals typical for chlorobutyl rubbers. It was observed that modification with polychlorinated n-alkanes improved the thermal and oxidative stability (the oxygen absorption rate decreased by 40%) and chemical resistance, estimated by the degree of swelling, which decreased with the increase in the chlorine content. This technology allows the production of a chlorinated rubber solution that can be directly used by rubber goods manufacturers and suppliers.

Synthesis of chlorinated butyl rubber by using sulfonyl chloride as chlorinating agent

Preparation and Properties of Bromochlorinated Butyl Rubber

Solvent Swelling-Induced Halogenation of Butyl Rubber Using Polychlorinated N-Alkanes: Structure and Properties

Study on Synthesis and Analysis of Methyltriacetoxysilane

Study on Addition Reaction of Benzenesulfonyl Chloride and Isoprene

Synthesis of high vinyl solution polymerized styrene-butadiene rubber with three-peak distribution using mixed coupling agents

Prompt Modification of Styrene‐butadiene Rubber Surface with Trichloroisocyanuric Acid by Increasing Chlorination Temperature

Cationic cyclization of styrene–butadiene rubber

In Situ Removal of HBr Via Microdroplets for High Selectivity Bromobutyl Rubber Synthesis in a Microreaction System

Effect of complex modifiers on polymerization kinetics and microstructure in synthesis of solution-polymerized styrene-butadiene rubber

Organic Interfacial Tailoring of Styrene Butadiene Rubber–clay Nanocomposites Prepared by Latex Compounding Method

MECHANOCHEMICAL MODIFICATION OF NITRILE-BUTADIENE RUBBER IN THE PRESENCE OF A CHLORINE-CONTAINING REAGENT

Experimental investigation on curing performance of neoprene rubber modified by BBr3

EFFECT OF HEATING ON STRUCTURAL PARAMETERS OF NITRILE BUTADIENE RUBBER IN THE PRESENCE OF CHLORINE-CONTAINING COMPOUNDS

Synthesizing Bromobutyl Rubber by A Microreactor System

Reinforced rubber with ionic liquid modified carbon black

Experimental investigation on curing performance of neoprene rubber modified by BBr_3

Synthesis of Sulphonic Lanthanum Complex Based on C-methylcalix[4]resorcinarene and Its Thermo-Oxidative Aging Resistance for Natural Rubber

A Study of the Ozonolysis of Butadiene Rubber in the Presence of Ethanol

Fabrication of Multifunctional Chitosan Derivative with Long-Chain Alkene and Thiourea Structure and Its Application in Styrene-Butadiene Rubber/Silica Composites

Synthesis, Properties of Novel Benzocyclobutene-Functionalized Siloxane Thermosets