Synthesis and properties of crosslinked waterborne polyurethane/acrylate copolymer latexes using AIBN initiator based on a solvent-/emulsifier-free method
Liu Qiang,Yu Yitao,Li Bing,Wang Jing,Sun Cuicui,Zhuang Haihua,Zhang Wei,Zong Jianping,Liu QiangYu YitaoLi BingWang JingSun CuicuiZhuang Haihua Zhang WeiZong Jianpinga Qilu University of Technology (Shandong Academy of Sciences),Advanced Materials Institute,Jinan,Chinab Department of Art and Design,Shandong Yingcai University,Jinan,Chinac Shandong Institute for Product Quality Inspection,Jinan,Chinad School of Chemical and Biological Engineering,QiLu Institute of Technology,Jinan,China
DOI: https://doi.org/10.1080/01694243.2023.2266208
IF: 2.431
2023-10-10
Journal of Adhesion Science and Technology
Abstract:In this study, a series of crosslinked waterborne polyurethane/acrylate copolymer latexes with different compositions were fabricated via emulsion polymerization using oil-soluble initiator (AIBN) based on a solvent-/emulsifiers-free method. Using the blend of styrene (St), butyl acrylate (BA) and crosslinkers (pentaerythritol triacrylate (PET3A) and pentaerythritol tetraacrylate (PET4A)) instead of acetone as a diluent and modifier, polyurethane prepolymers terminated with hydroxyethyl acrylate composite emulsions were prepared using polypropylene glycol (PPG), toluene diisocyanate (TDI), 2,2-dihydroxymethylpropionic acid (DMPA) and diethylene glycol (DEG) without other solvents. It was found that for all the emulsion polymerization of waterborne polyurethane and acrylates initiated by AIBN, the monomer conversions exceeded 96% when the concentration of AIBN was in the range of 0.5% to 0.9% (w/w) and the optimal reaction temperature was 75 °C. The introduction of St, BA and crosslinkers would form the polymer network, improving the tensile strength, water absorption of the copolymer latex films. Dynamic light scattering analyses showed that the copolymer latexes exhibited a unimodal distribution and showed no precipitates and unstable aggregates. The average particle size distribution was in the range of 131–154 nm. Transmission electron microscopy studies have confirmed the similar results and the latex particles possessed the core–shell morphology structure.
materials science, multidisciplinary,engineering, chemical,mechanics