Abstract:Keto-hydrazide cross-linking chemistry between diacetone acrylamide (DAAM) and adipic acid dihydrazide (ADH) has been widely applied in conventional emulsion polymerization to render materials with specific chemical and physical properties. However, significant drawbacks are usually associated with the conventional process, such as the migration of low-molar-mass surfactants, and the low cross-linking efficiency due to the random distribution of the cross-linkers throughout the nanoparticles. We demonstrate here the concept of surface cross-linking of latexes in a RAFT-mediated surfactant-free procedure that overcomes the migration of surfactants while improving the cross-linking efficiency of latexes. Specifically, the “surface cross-linking” here refers to the cross-linking of colloidal particles’ surfaces during the film formation process. First, an amphiphilic RAFT agent with the incorporation of a cross-linking unit (DAAM) was designed and synthesized; the following controlled emulsion polymerizations provide a series of surfactant-free latexes with excellent colloidal stabilities, high solid contents (>40.0 wt %), and a size range of 150–250 nm. To access RAFT latexes with different cross-linking degrees and mechanisms, amphiphilic RAFT agents with different units of cross-linking component (DAAM) were designed and implemented for the controlled emulsion polymerization of styrene and n-butyl acrylate. Next, the surface cross-linkable and randomly cross-linkable RAFT latexes and corresponding films were prepared. It was found that the surface cross-linked films exhibited not only improved Young’s modulus and storage modulus but also better solvent resistance compared to the control group with DAAM units randomly distributed throughout the particle systems. Remarkably, it was noticed that the surface cross-linking process can simultaneously increase the strain at break and ultimate stress, and this is the first observation of such a phenomenon in DAAM/ADH cross-linked latex films. Overall, this study represents the first attempt that combines surfactant-free RAFT-mediated emulsion polymerization with the surface cross-linking chemistry to produce cohesive films with enhanced and tunable mechanical properties. This universal synthetic strategy is applicable to a broad range of commercial monomers and can be used as a platform technology for advanced industrial applications.

The crosslinking directing dynamic behavior of polymer latex under the investigation toward waterborne damping coatings

Stability of the emulsion copolymerization process of the latex containing glycidyl and amino groups

Styrene–Acrylic Emulsion with “Transition Layer” for Damping Coating: Synthesis and Characterization

Study on Damping Properties of Acrylate Latex Copolymer

Preparation of styrene–butyl acrylic latex films with impact resistance properties and their applications as water-based damping coating

Preparation and damping properties of polyacrylate and epoxy resin/polyacrylate composite latex materials

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Synthesis and Performance of A Self Crosslinkable Acrylate Copolymer with High Compatibility for an Oil Well Cement Modifier

The Effect of Macromonomer Surfactant Microstructure on Aqueous Polymer Dispersion and Derived Polymer Film Properties

ENHANCEMENT OF DAMPING PERFORMANCE OF POLYMERS BY FUNCTIONAL SMALL MOLECULES

Hydroxyl‐terminated polybutadiene based waterborne polyurethane acrylate emulsions: Synthesis, characterization, and damping property

Studies on the damping performance of polystyrene/polyacrylate latex IPN

Manipulation of chain transfer agent and cross-linker concentration to modify the performance of fluorinated acrylate latex pressure sensitive adhesive

Nanoparticle Surface Cross-Linking: A Universal Strategy to Enhance the Mechanical Properties of Latex Films

Synthesis and characterization of crosslinkable latex with interpenetrating network structure based on polystyrene and polyacrylate

Preparation and characterization of fluorocarbon latex modified by diallyl malate

Preparation of low‐temperature self‐crosslinking acrylic resin and its performance research

Study on damping properties of acrylate LIPN polymer

Waterborne polyurethane acrylate emulsion with dangling chain structure: Simultaneously showing wide damping temperature range and excellent hydrophobic performance

Controllable Design and Synthesis of Polyurethane Elastomers Containing Polar Dangling Chains with High Mechanical Properties and Wide Damping Temperature Range

Controllable Design and Preparation of Hydroxyl-Terminated Solution-Polymerized Styrene Butadiene for Polyurethane Elastomers with High-Damping Properties