Property and Technology of Zn-Cr Coating on Sintered NdFeB Permanent Magnet

Yu Shengxue,Chen Ling

DOI: https://doi.org/10.3321/j.issn:1000-4343.2006.01.013

2006-01-01

Abstract:Zn-Cr coating was obtained on the surface of sintered NdFeB permanent magnet by special solution immersion,removing excess solution,baking at 80±5 ℃ for 20 min and sintering at 290～310 ℃ for 30 min.The suitable conditions of the technology were established.The corrosion-resistant property of the coating was studied by 3.5% salt solutions immersion test and compared with plating zinc and plating nickel on the surface of NdFeB permanent magnet.The corrosion-resistant property of Zn-Cr coating is significantly superior to that of Zn and Ni coating.The φ_(corr) and j_(corr) of the bare sample and Zn-Cr coating sample were examined by electrochemical method in 3.5% salt solutions respectively.The result shows that the value of φ_(corr) of Zn-Cr coating is less than that of bare NdFeB substrate,and Zn-Cr coating makes sacrifice to protect NdFeB substrate as anode in corrosion medium.The microphotography of surface and cross section of the coating were observed by SEM.The results show that Zn-Cr coating is covered even on the surface of the substrate and Zn flakes lay nearly parallel to matrix,which discourage corrosive medium from attacking the substrate.The composition of coating was investigated by means of XRD,XPS and EDS. The test results indicate that the coating consists of Zn(0),Zn(Ⅱ),Cr(Ⅲ) and a little Cr(Ⅵ),and the Cr(Ⅵ) possesses passivation function to Zn flake and NdFeB substrate.Therefore,the NdFeB after Zn-Cr coating treatment processes get high corrosion-resistant property.And the coating has no negative effects on magnetic properties.