Abstract:Nanocrystalline diamond (NCD) films are attractive for many applications due to their smooth surfaces while holding the properties of diamond. However, their growth rate is generally low using common Ar/CH4 with or without H2 chemistry and strongly dependent on the overall growth conditions using microwave plasma chemical vapor deposition (MPCVD). In this work, incorporating a small amount of N2 and O2 additives into CH4/H2 chemistry offered a much higher growth rate of NCD films, which is promising for some applications. Several novel series of experiments were designed and conducted to tailor the growth features of NCD films by fine-tuning of the gas-phase compositions with different amounts of nitrogen and oxygen addition into CH4/H2 gas mixtures. The influence of growth parameters, such as the absolute amount and their relative ratios of O2 and N2 additives; substrate temperature, which was adjusted by two ways and inferred by simulation; and microwave power on NCD formation, was investigated. Short and long deposition runs were carried out to study surface structural evolution with time under identical growth conditions. The morphology, crystalline and optical quality, orientation, and texture of the NCD samples were characterized and analyzed. A variety of NCD films of high average growth rates ranging from 2.1 μm/h up to 6.7 μm/h were successfully achieved by slightly adjusting the O2/CH4 amounts from 6.25% to 18.75%, while that of N2 was kept constant. The results clearly show that the beneficial use of fine-tuning of gas-phase compositions offers a simple and effective way to tailor the growth characteristics and physical properties of NCD films for optimizing the growth conditions to envisage some specific applications.

CVD Grow of Nano Diamond and Other Carbon Materials on Porous Carbon

Growth of Nanocrystalline Diamond Films on Co-Cemented Tungsten Carbide Substrates by Hot Filament CVD

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Synthesis and Mechanism Study of Carbon Nanowires, Carbon Nanotubes, and Carbon Pompons on Single-Crystal Diamonds

Growth of ultrananocrystalline diamond film by DC Arcjet plasma enhanced chemical vapor deposition

Growth of One Dimensional Nanocarbons on Bamboo Based Porous Carbon

Using active carbon pellet as substrate for deposition diamond by MPCVD

The Effect of Depositing Time on the Mpcvd of Diamond on Porous Carbon Monolith

The Growth And Interface Characteristics Of Diamond Films On Cemented Carbide Substrates

Diamond Films and Particles Growth in Hydrogen Microwave Plasma with Graphite Solid Precursor: Optical Emission Spectroscopy Study

Fast, Efficient Tailoring Growth of Nanocrystalline Diamond Films by Fine-Tuning of Gas-Phase Composition Using Microwave Plasma Chemical Vapor Deposition

Growth of single-crystal diamond by microwave plasma CVD with high precursor utilization using cyclic gas injection and control of carbonaceous species content with optical emission spectroscopy

High quality CVD single crystal diamonds grown on nanorods patterned diamond seed

Synthetic Hierarchical Nanostructures: Growth of Carbon Nanofibers on Microfibers by Chemical Vapor Deposition

Growth and morphological studies of (100) textured diamond thin films by microwave plasma-enhanced chemical vapor deposition

Preparation of Diamond Films by Hot Filament Chemical Vapor Deposition and Nucleation by Carbon Nanotubes

Nanocrystalline Diamond Film Grown by Pulsed Linear Antenna Microwave CVD

Enhanced Nucleation and Growth of Diamond Film on Si by CVD Using a Chemical Precursor

Synthesis of Nanocrystalline Diamond Films on Smooth Wc-Co Cemented Carbide Substrates

Effect of Nano-Ni Catalyst on the Growth and Characterization of Diamond Films by HFCVD

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD