Tabular Sr3Ti2O7 Intermediates Synthesized by Molten Salt Method

Lin-hong CAO,Wei-dong WU,Zhen ZHANG,Zhuo XU,Guang-liang XU

DOI: https://doi.org/10.3969/j.issn.1004-2474.2009.03.029

2009-01-01

Abstract:Using SrCO3 and TiO2 as raw materials,the tabular intermediates Sr3Ti2O7 was synthesized by molten salt method.The phase composition and microstructure of these powders were analyzed by X-ray diffraction(XRD) and scanning electron microscopy(SEM).The effects of molten salt(NaCl and KCl),reactive temperature and reactive time on the synthesis of tabular intermediates Sr3Ti2O7 were discussed in this paper.The results showed that the intermediates obtained by using KCl as molten salt were composed of anisotropic Sr3Ti2O7 and Sr2TiO4.The intermediates obtained by using NaCl as molten salt were composed of anisotropic Sr3Ti2O7,Sr2TiO4 and Sr4Ti3O10.There have little effect on phase composition and phase contents by using excessive SrCO3 or improving synthesis temperature.Moreover,by using excessive SrCO3 or improving synthesis temperature,the contents of Sr3Ti2O7 increase,but that of Sr2TiO4 decreases.The intermediates obtained at 1 300 ℃ for 4 h by using NaCl as molten salt were rectangle and tabular,its edge length and thickness is 30~60 μm and 2~5 μm respectively,which is the idea template for epitaxial growth of <001>SrTiO3 tabular crystals.However,the intermediates obtained by using KCl as molten salt were also rectangle and tabular,its edge length and thickness is 10~20 μm and 5~10 μm.