Abstract:In this work, BaTiO3 powders were synthesized by molten-salt synthesis method using BaCO3, TiO2, and the eutectic salts (NaCl-KCl) as the raw materials. A systematic study indicating the effects of calcination temperature as well as the molar ratio of NaCl to KCl in the mixed salt with respect to BaCO3-TiO2 on the microstructures of BaTiO3 powders is reported. The results showed that all the powders crystallized in a tetragonal perovskite structure, as confirmed by X-ray diffraction pattern and Raman spectra. With increasing the calcination temperature, the morphology of the as-prepared BaTiO3 powders developed from rectangular/spherical aggregates to circular or cubic shapes and the average particle size was also increased from 320 nm to 900 nm. With increasing the molar ratio of BaCO3: TiO2: NaCl: KCl, the average particle size was slightly decreased from 440 nm to 360 nm, and the morphology of the as-synthesized BaTiO3 powders transformed from rectangular and cubic shapes to sphere shapes. The chemical compositions of the as-synthesized BaTiO3 powders obtained from energy dispersive X-ray analysis are in agreement with the nominal ratios. The present results provide a generalized methodology to large-scale synthesize other perovskite transitional metal oxide powders with controllable sizes and shapes. (C) 2016 Elsevier B.V. All rights reserved.

Tabular SrTiO3 Synthesized by Two-Step Molten Salt Method

Tabular Sr3Ti2O7 Intermediates Synthesized by Molten Salt Method

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Synthesis of CaCu3Ti4O12 Micron-cubes and rods via high proportion molten salt method

Self-assembly and formation mechanism of single-crystal SrTiO3 nanosheets via solvothermal route with ethylene glycol as reaction medium

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Synthesis of mesoporous strontium titanate by molten salt assisted template-free method

Solvothermal synthesis, characterization and formation mechanism of single-crystalline SrTiO3 dense spheres with monoethanolamine as reaction medium solvent

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

EG-solvothermal Synthesis of Self-Assembly SrTiO3 Nano Sheets and Photocatalytic Property

Synthesis of Ba0.6Sr0.4TiO3 Platelet Crystals Based on Bi4Ti3O12 Precursor by Topochemical Microcrystal Conversion

Synthesis of Single-Crystal Ba1−xSrxTiO3 (x = 0–1) Dendrites Via a Simple Hydrothermal Method

Solution Synthesis and Growth Mechanism of SrTiO3mesocrystals

Synthesis of textured Li0.33La0.55TiO3 solid electrolytes by molten salt method

Metal-Organic Chemical-Vapor Deposition of (ba,sr)tio3: Nucleation and Growth on Pt-(111)

Synthesis of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 powders through the molten salt method

Synthesis of Large Diameter Plat-Like Ca3co4o9 Particle by Molten Salt Method

Top-seeded solution growth of SrTiO3 crystals and phase diagram studies in the SrO-TiO2 system

Synthesis and Characterization of Fibrous SrTiO3 Particles

Molten flux growth of single crystals of quasi-1D hexagonal chalcogenide BaTiS3