Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Synthesis of Crystalline Sic Nanofiber Through the Pyrolysis of Polycarbomethylsilane Coated Platelet Carbon Nanofiber

Ultrafast growth of single-crystalline Si nanowires

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Effect of Impurities Control on the Crystallization and Densification of Polymer-Derived SiC Fibers

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Fabrication and characterization of pyrolytic carbons from phenolic resin reinforced by SiC nanowires with chain-bead structures

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

Large Areas of Centimeters-Long SiC Nanowires Synthesized by Pyrolysis of a Polymer Precursor by a CVD Route

Effect of crystallinity of PAN-based carbon fiber surfaces on the formation characteristics of silicon carbide coating

Polycrystalline Nanograin Formation in Uniform-Sized Silicon Carbide Fibers Derived from Aluminum-Containing Polycarbosilane

Synthesis of Silicon Carbide Nanorods by Catalyst-Assisted Pyrolysis of Polymeric Precursor

Synthesis of Polytitanocarbosilane and Preparation of Si–C–Ti–B Fibers

EFFECT OF PYROLYSIS TEMPERATURE ON MICROPORE SIZE DISTRIBUTION IN SILICON CARBIDE FIBERS BY THE SMALL ANGLE X-RAY SCATTERING

Controlled growth of SiC crystals in combustion synthesis

Preparation, Characterization and Growth Mechanism of Platelet Carbon Nanofibers

Synthesis of SiC/SiO2 core–shell nanowires with good optical properties on Ni/SiO2/Si substrate via ferrocene pyrolysis at low temperature

Superparamagnetic Silicon Carbonitride Ceramic Fibers Through In Situ Generation of Iron Silicide Nanoparticles During Pyrolysis of an Iron-Modified Polysilazane

Synthesis and characteristics of polycarbomethylsilane via a one-pot approach

Elemental and structural evolution of polymer-derived SiC fibers fabricated via solution blend and iodine curing methods

A Simple Route to Nanocrystalline Silicon Carbide