Abstract:Abstract In this study, the high-density SiC/SiO 2 core–shell nanowires were synthesized on the nickel coated SiO 2 (100 nm)/Si substrate by chemical vapor deposition (CVD) method with ferrocene precursor at temperature 1000 °C compared to previous studies (1300–1600 °C). The present work provides an efficient strategy for the production of SiC/SiO 2 nanowires with uniform morphology and good optical properties, where the Ni layer plays important roles for this fabrication at low temperature which reduces the decomposition temperature of hydrocarbon gases and improves the growth quality of SiC nanowires. The as-synthesized SiC/SiO 2 nanowires consist of single crystal 3C structures as well as 3C structures with defects along [111] direction. In the photoluminescence (PL) spectrum, the SiC/SiO 2 core–shell nanowires revealed an obvious blueshift. The blueshift is due to the formation of nanoscale silicon carbide polytypism caused by the stacking faults in 3C–SiC and the nanoscale polytypism also caused the transition from indirect to direct bandgap which explains why the stacking faults percentage in SiC confirmed from X-ray diffraction (XRD) is 19%, but ultimately makes the strongest emission intensity. Finally, the PL characteristics are further improved by changing the diameter of the SiC nanowire and etching and an approximate model followed by the vapor–liquid–solid (VLS) mechanism was proposed to explain the possible growth mechanism of the SiC/SiO 2 nanowires.

Large Areas of Centimeters-Long SiC Nanowires Synthesized by Pyrolysis of a Polymer Precursor by a CVD Route

Ultrafast growth of single-crystalline Si nanowires

Morphology-Controlled Synthesis of SiC Nanowires by Catalyst-Assisted Pyrolysis of Polymeric Precursor

Synthesis of Silicon Carbide Nanorods by Catalyst-Assisted Pyrolysis of Polymeric Precursor

Preparation and Characterization of Bundled One-Dimensional Si3N4 Single-Crystalline Nanowires by Catalytic Pyrolysis of a Polymer Precursor

Continuous Preparation of SiC Nanowires Using Fluidized Bed Chemical Vapor Deposition Method

Ultralong Single Crystal Silicon Nanowires Synthesized by Chemical Vapor Deposition

Silicon Carbide Nanowires Synthesized with Phenolic Resin and Silicon Powders

Adjusting the Morphology and Properties of SiC Nanowires by Catalyst Control

Synthesis of SiC/SiO2 core–shell nanowires with good optical properties on Ni/SiO2/Si substrate via ferrocene pyrolysis at low temperature

Ultra‐Long Single‐Crystalline Α‐si3n4nanowires: Derived from a Polymeric Precursor

Preparation of Highly Flexible SiC Nanowires by Fluidized Bed Chemical Vapor Deposition

Synthesis of large-scale SiC@SiO2 nanowires with good optical properties by using Si@SiO2 as silicon source

Facile growth of oriented SiC nanowires arrays on carbon fiber cloth via CVD

Triangular prism-shaped p-type 6H-SiC nanowires

Synthesis of High-Purity SiC Nanowires via Catalyst-Free Pyrolysis of SiO 2 /Si and Sponge-Like Graphene Oxide

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation

Fabrication and characterization of pyrolytic carbons from phenolic resin reinforced by SiC nanowires with chain-bead structures

Large-scale synthesis and characterization of hexagonal prism-shaped SiC nanowires.

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process