Abstract:SiC reinforced Al (SiC/Al) composites have outstanding advantages in different fields including aerospace. However, the current mechanical and chemical properties of Al–SiC composites are still not up to expectations because of the problems such as wettability, interface reaction, sintering time and SiC size and distribution. Microwave rapid sintering has a promising prospect for the preparation of high performance Al–SiC, however, the lack of process observation leads to the unclear relationship of energy, microstructure and material properties. Therefore microwave rapid sintering of Al–SiC has not been fully explored and applied. In the present paper, the whole process of Al–SiC microstructure evolution was observed accurately by in situ SR-CT experiment during microwave rapid sintering process. Based on the joint analysis of energy-structure-performance, it was found that the spherical SiC located at the neck of Al particles in the microwave field effectively increased the diffusion rate of Al–SiC samples, which inhibited the growth of grains and the densification process was basically completed in a short time. It was revealed that a region with high electric field strength and uniform distribution formed due to SiC with different structural characteristics, thus achieved the rapid densification of the Al–SiC in microwave sintering. The formation and regulation mechanism of rapid densification of Al–SiC during microwave rapid sintering were researched by the relationship between energy-structure and performance, which would provid more understanding for the preparation of high-performance Al–SiC based on microwave rapid sintering technology, and provide the possibility for the preparation of more functional materials.

Rapid manufacture of net-shape SiC components

Rapid Manufacture of High Relative-density and Complex Structure Components of Silicon Carbide by RMI-PIP Process

Rapid Fabrication of C/C-Sic Composites

Reaction-bonded SiC Derived from Resin Precursors by Stereolithography

A new approach for the net-shape fabrication of porous Si3N4 bonded SiC ceramics with high strength

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Manufacturing Silicon Carbide Microrotors by Reactive Hot Isostatic Pressing within Micromachined Silicon Molds

Silicon Carbide Micro-Reaction-Sintering Using Micromachined Silicon Molds

Gel Reactive Melt Infiltration: A New Method for Large-Sized Complex-Shaped C/C Components Ceramic Modification

A Low Cost Preparation of C/SiC Composites by Infiltrating Molten Si into Gelcasted Pure Porous Carbon Preform

Study on Novel Procedure for Complex-shaped SiC Ceramic Components

Rapid and cost-effective fabrication of SiC from Si scrap through flash sintering

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Reaction Forming of Silicon Carbide Ceramic Using Phenolic Resin Derived Porous Carbon Preform

Rapid Fabrication of C/C/SiC Composite by PIP of HMDS

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform

Fabrication of low-shrinkage, porous silicon nitride ceramics by addition of a small amount of carbon

In Situ SR-CT Experiment of Al–SiC Microwave Rapid Sintering: Formation and Regulation of Rapid Densification

High‐strength Si–SiC lattices prepared by powder bed fusion, infiltration‐pyrolysis, and reactive silicon infiltration

Preparation of Complex-Shape SiC Ceramic Composites Parts Derived from Phenolic Resin Template

Preparation of low residual silicon content Si-SiC ceramics by binder jetting additive manufacturing and liquid silicon infiltration