Abstract:Selective laser sintering (SLS) combined with reaction melt infiltration was used to fabricate Si–SiC ceramic matrix composites, and the effects of different concentrations of phenolic resin (PF) on the properties of the SLS green body and carbonized and final Si–SiC samples were investigated. The results showed that the impregnation with PF can increase the bulk density, reduce the porosity of the samples at all stages, and improve the mechanical properties of the reactive bonded samples. The degree of densification and mechanical properties of the sample gradually enhanced with an increase in PF concentration. The main phases of the Si–SiC composites were free Si, α-SiC, β-SiC, plus an extremely small amount of Al–Si alloy, and the SiC and the Si phase contents increased and decreased, respectively, as the concentration of PF increased when measured using Rietveld refinement and image analysis software. The macroscopic properties of the samples improved greatly after precursor infiltration pyrolysis (PIP) treatment with 66.7%vol PF-ethanol solution twice. According to the crystal nucleation-growth theory, it was inferred that the infiltrated PF could provide a certain amount of pyrolytic carbon in the carbonized specimen. During the reaction bonded process, the carbon formed by carbonization pyrolysis first dissolves into the molten Si and reaches saturation. With the further dissolution of carbon, [C] and [Si] in the liquid phase contact each other to form β-SiC nuclei, the nuclei that precipitate at the pore wall position and gradually form a continuous interfacial layer of β-SiC. The β-SiC layer prevents the liquid Si from direct contact with C inside the prefabricated body, therefore, further reactants diffuse through the layer. Finally, the fine crystalline β-SiC grains were fabricated inside the specimen.

Reaction Forming of Silicon Carbide Ceramic Using Phenolic Resin Derived Porous Carbon Preform

Preparation of Complex-Shape SiC Ceramic Composites Parts Derived from Phenolic Resin Template

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform

Preparation of Reaction-Formed Porous SiC Ceramics

Reaction-bonded SiC Derived from Resin Precursors by Stereolithography

Formation Mechanism of Porous Silicon Carbide Ceramic Synthesized by Coat-Mix Process

Preparation and characterization of porous, biomorphic SiC ceramic with hybrid pore structure

PREPARATION OF MACROPOROUS SiC FROM WOODCERAMICS AND SILICON POWDER BY IN SITU REACTION-SINTERING PROCESS

Effect of impregnated phenolic resin on the properties of Si–SiC ceramic matrix composites fabricated by SLS-RMI

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Properties regulation of SiC ceramics prepared via stereolithography combined with reactive melt infiltration techniques

A Low Cost Preparation of C/SiC Composites by Infiltrating Molten Si into Gelcasted Pure Porous Carbon Preform

Processing of silica bonded porous SiC preform for metallic composites

Microstructure Evolution and Reaction Mechanism of Microporous Carbon Derived SiC Ceramic

Fabrication and Characterization of Hierarchical Porous SiC Ceramics Via Gelcasting and Carbothermal Reduction Between Carbon and SiO

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Preparation and Basic Properties of a New Porous SiC

Preparation and Formation Mechanism of C/C–SiC Composites Using Polymer-Si Slurry Reactive Melt Infiltration

Microstructure Evolution Process of Porous Silicon Carbide Ceramics Prepared Through Coat-Mix Method

THE PREPARATION OF SiC POROUS CERAMIC PREFORMS

Microstructure Evolution and Performance Improvement of Silicon Carbide Ceramics via Impregnation Method