Abstract:This study aims to investigate the role of hydrogen on CNTs synthesis and kinetics of CNTs formation. The CNTs were synthesized by catalytic chemical vapor deposition of methane over FeMo/MgO catalyst. The experimental results revealed that hydrogen plays an important role in the structural changes of catalyst during the pre-reduction process. The catalyst structure fully transformed into metallic FeMo phases, resulting in an increased yield of 5 folds higher than those of the non-reduced catalyst. However, the slightly larger diameter and lower crystallinity ratio of CNTs was obtained. The hydrogen co-feeding during the synthesis can slightly increase the CNTs yield. After achieving the optimum amount of hydrogen addition, further increase in hydrogen would inhibit the methane decomposition, resulting in lower product yield. The hydrogenation of carbon to methane was proceeded in hydrogen co-feed process. However, the hydrogenation was non-selective to allotropes of carbon. Therefore, the addition of hydrogen would not benefit neither maintaining the catalyst stability nor improving the crystallinity of the CNT products. The kinetic model of CNTs formation, derived from the two types of active site of dissociative adsorption of methane, corresponded well to the experimental results. The rate of CNTs formation greatly increases with the partial pressure of methane but decreases when saturation is exceeded. The activation energy was found to be 13.22 kJ mol −1 , showing the rate controlling step to be in the process of mass transfer.

An essential role of CO2 and H2O during single-walled CNT synthesis from carbon monoxide

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

Carbon Dioxide Promotes Dehydrogenation in the Equimolar C2 H2 -CO2 Reaction to Synthesize Carbon Nanotubes.

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Low-temperature synthesis of multi-walled carbon nanotubes over Cu catalyst

Synthesis of Multi-wall Carbon Nanotubes Using Fe/CNTs As Catalyst

Carbon Nanotubes: in Situ Monitoring the Role of Working Metal Catalyst Nanoparticles for Ultrahigh Purity Single‐Walled Carbon Nanotubes (adv. Funct. Mater. 40/2013)

Catalytic Mechanism of Co-containing Layered Double Hydroxide (Co-LDH) as a Precursor in Carbon Nanotube (CNT) Synthesis

Preparation of multi-walled carbon nanotubes using NiO catalyst synthesized by hydrothermal method

Carbon monoxide-assisted growth of carbon nanotubes

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Synthesis of MWCNTs by chemical vapor deposition of methane using FeMo/MgO catalyst: role of hydrogen and kinetic study

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Gas-induced formation of Cu nanoparticle as catalyst for high-purity straight and helical carbon nanofibers.

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C

Combination effect of growth enhancers and carbon sources on synthesis of single-walled carbon nanotubes from solid carbon growth seeds

Syntheses of carbon nanomaterials by radio frequency plasma enhanced chemical vapor deposition

Optimization of Synthesis Conditions of Carbon Nanotubes via Ultrasonic-Assisted Floating Catalyst Deposition Using Response Surface Methodology

Synthesis of Carbon Nanotubes by Catalytic Chemical Vapor Deposition Using Hydrogen Storage Alloy As A Catalyst

Synthesis of Helical Carbon Nanotubes, Worm-Like Carbon Nanotubes and Nanocoils at 450 °C and Their Magnetic Properties