Abstract:Using Fe-MgO, Co-MgO and Ni-MgO catalysts preparated by citric acid method, carbon nanotubes (CNTs) were synthesized from decomposition of methane at 873 K, 973 K and 1013 K, respectively, and were characterized by TEM and Raman spectra. The effects of catalysts, preparation temperature and reaction time on the shape, yield and inter - structure of carbon nanotubes were discussed.TEM results and Raman spectra show that the shapes and inter-structures of carbon nanotubes produced on different catalysts at the same temperature are quite different. Carbon nanotubes synthesized on Fe-MgO incline to be rods, with very thick wall, and the diameter varied greatly from 10 nm to 80 nm. However, the diameter of carbon nanotubes produced on Co-MgO is about 35 nm, and about 20 nm on Ni-MgO. As can see from the Raman spectra, the G peaks of carbon nanotubes produced on the three catalysts shift slightly, which indicate the difference of the inter-structure of nanotubes.The experiments show that the yield of carbon nanotubes varied with decomposition temperature. Using Fe-MgO catalysts, yield of carbon nanotubes grows with the decomposition temperature. However, using Ni-MgO catalysts, the yield drops when the temperature increases. The reaction temperature with the largest yield of carbon nanotubes is higher than 1013 K on Fe-MgO catalysts, about 973 K on Co-MgO catalysts, and lower than 873 K on Ni-MgO catalysts, respectively.The results also show that the yield of carbon nanotubes does not increase with the decomposition time. There is a saturation time of the carbon nanotube growth. The carbon nanotubes do not grow any more when the saturation time reaches. For example, on Ni-MgO catalysts, the carbon nanotubes stop growing after decomposition of CH4 for 2 h.

Synthesis of Multi-wall Carbon Nanotubes Using Fe/CNTs As Catalyst

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

Low-temperature synthesis of multi-walled carbon nanotubes over Cu catalyst

Synthesis of Carbon Nanotubes by Decomposing Alcohol

SYNTHESIS OF CARBON NANOTUBES USING Fe-LOADING MESOPOROUS MOLECULAR SIEVES AS TEMPLATES

The influence of ethanol on the growth and structure of carbon nanotubes

Synthesis and growth of multi-walled carbon nanotubes (MWNTs) by CCVD using Fe-supported zeolite templates

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

Synthesis of Carbon Nanotubes Via Fe-Catalyzed Pyrolysis of Phenolic Resin

Synthesis of multiwalled carbon nanotubes on fly ash derived catalysts.

High-Yield Production of Multi-Walled Carbon Nanotubes by Catalytic Decomposition of Benzene Vapor

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

The Factors of Preparation of Carbon Nanotubes by Catalytic Decomposition of Methane

Catalytic Preparation of Carbon Nanotubes from Waste Polyethylene Using FeNi Bimetallic Nanocatalyst.

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Synthesis of Fe-Al catalysts to boost CNTs formation from polymer wastes via the improved two-stage system

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C