Abstract:C/CMS composite membranes from poly(furfuryl alcohol) for gas separation were successfully prepared, in which porous coal-based carbon tubes with an average pore diameter of 0.11μm and a porosity of 40.3% were used as support. The tubular support was coated using viscous poly(furfuryl alcohol) liquid to form an organic layer that was transformed into a thin top layer of carbon membrane after pyrolysis. The gas separation performance of the as-prepared carbon membranes was evaluated at 25, 60 and 80°C by molecular probe method. The morphology and structure changes of C/CMS composite membranes during pyrolysis were examined using SEM, HRTEM, FTIR and XRD techniques. The results show that C/CMS composite membranes with uniform and defect-free thin top layer can be made by one-step coating with viscous poly(furfuryl alcohol) liquid and following pyrolysis. The as-prepared C/CMS composite membranes have excellent gas separation properties for gas pairs such as H2/N2, CO2/N2, O2/N2 and CO2/CH, and the highest permselectivity at 25°C can reach up to 465.0, 58.8, 13.2 and 160.5, respectively. It has been found that the permeabilities of the composite membranes decrease while the permselectivities increase as the pyrolysis temperature increases from 300 to 700°C. During pyrolysis, the polymeric structure of poly(furfuryl alcohol) has been transformed into an amorphous turbostratic carbon structure with ultramicropores. For the as-prepared C/CMS composite membranes, the gas separation performance in this work exhibits great competition respect to other carbon membranes reported. These clearly indicate that the C/CMS composite membranes prepared from furfuryl alcohol polymers is a promising membrane for gas separation.

Preparation of Tubular Composite Carbon Membrane for Gas Separation

Preparation of A Plate-Like C/C Composite Membrane for Gas Separation

Preparation of PPESK based composite carbon membrane for gas separation

Preparation and applications of coal-based tubular carbon membranes

Preparation and Gas Separation Properties of Poly(Furfuryl Alcohol)-Based C/Cms Composite Membranes

Selective Permeation of CO2 Through a Composite Membrane with a Separation Layer of 2-N,n-dimethyl Aminoethyl Methacrylate and Acrylic Acid Copolymer

Preparation and Gas Separation Performance of Composite Carbon Molecular Sieve Membrane from the Polyester Precursor

Pebax-derived Ultra-Microporous Carbon Molecular Sieve Composite Membrane Assisted by Organic Interlayer for Gas Separation

Zeolite L/carbon Nanocomposite Membranes on the Porous Alumina Tubes and Their Gas Separation Properties

Carbon membrane for gas separation derived from coal tar pitch

Preparation and Characterization of Carbon Membrane from BDAF-PMDA Polyimide

Thin Zeolite T/Carbon Composite Membranes Supported on the Porous Alumina Tubes for Co2 Separation

Preparation of PDMS Composite Membranes with Flexible Supports and Their Performance in C3 Hydrocarbon Gases/N2 Separation

Physical Design, Preparation and Functionalization of Carbon Membranes for Gas Separation

Preparation of a PVA/Chitosan/Glass Fiber Composite Membrane and the Performance in CO2 Separation

Preparation Of Ni-P Alloy Composite Tube-Form Carbon Membrane For Gas Separation

Physical Design, Preparation and Functionalization of Carbon Membranes for Gas Separation: Physical Design, Preparation and Functionalization of Carbon Membranes for Gas Separation

Thin Carbon/sapo-34 Microporous Composite Membranes for Gas Separation

Carbon molecular sieve hollow fiber composite membrane derived from PMDA-ODA polyimide for gas separation

Preparation of Polyvinylamine/polysulfone Composite Hollow‐fiber Membranes and Their CO2/CH4 Separation Performance

A High CO2 Permselective Mesoporous Silica/carbon Composite Membrane for CO2 Separation