Abstract:Hydrogen (H2) has become one of the promising alternative clean energy resources. Membrane technology is a potential method for hydrogen separation or production. This study aims to develop a new carbon membrane for hydrogen separation or production. Moreover, the permeation behavior of H2, CO2, and CH4 through a hollow fiber composite carbon membrane derived from P84 co-polyimide and with incorporation of zeolite composite carbon (ZCC) was also examined. ZCC was synthesized via the impregnation method of sucrose into zeolite-Y pores, followed by carbonization at 800 °C. Thus, this filler has a high surface area, high microporosity, ordered pore structure, and low hydrophilicity. The presence of zeolites in ZCC is predicted to increase certain gases' affinity for the membrane. Various heating rates (1-5 °C/min) were applied during pyrolysis to understand the effect of the heating rate on the pore structure and H2/CO2 and H2/CH4 gas separation performance. Moreover, gas permeation was evaluated at various temperatures (298-373 K) to study the thermodynamic aspect of the process. A characteristic graphite peak was detected at 2θ ∼ 44° in all carbon samples. Scanning electron microscopy (SEM) observations revealed the void-free surface and the asymmetric structure of the carbon membranes. During the permeation test, it was found that gas permeation through the membrane was significantly affected by the temperature of the separation process. The highest permeability of H2, CO2, and CH4 was detected on the composite carbon membrane at a 3 °C/min heating rate with a permeation temperature of 373 K. The thermodynamic study shows that CO2 and H2 have lower activation energies compared to CH4. The transport mechanism of the membrane involved adsorption and activated surface diffusion. The permeation temperature has a large impact on the transport of small penetrants in the carbon matrix.

Preparation Of Ni-P Alloy Composite Tube-Form Carbon Membrane For Gas Separation

Preparation of continuous NH2–MIL-53 membrane on ammoniated polyvinylidene fluoride hollow fiber for efficient H2 purification

Stiff Metal–organic Framework–polyacrylonitrile Hollow Fiber Composite Membranes with High Gas Permeability

Preparation and characterization of NiP amorphous alloy/ceramic composite membrane

Nanofibers Interpenetrating Network Mimicking “Reinforced-Concrete” to Construct Mechanically Robust Composite Membrane for Enhanced CO2 Separation

A Novel Ni-Ru-P Amorphous Alloy Composite Membrane and Its Performance Study

Selective Permeation of CO2 Through a Composite Membrane with a Separation Layer of 2-N,n-dimethyl Aminoethyl Methacrylate and Acrylic Acid Copolymer

Polymide/Fe_3O_4-carbonized Membranes for Gas Separation

Preparation of PDMS/PVDF composite membrane and its application in C_3H_8/N_2 separation

Preparation of carbon molecular sieve membrane derived from phenolic resin over macroporous clay-alumina based support for hydrogen separation

CO2/N2 Separation Using Polyvinyl Chloride Iso-Phthalic Acid/Aluminium Nitrate Nanocomposite Membrane

Preparation of a PVA/Chitosan/Glass Fiber Composite Membrane and the Performance in CO2 Separation

Thermal Stability, Hydrogen Adsorption and Separation Performance of Ni-based Amorphous Alloy Membranes

Fabrication of polyarylate thin-film nanocomposite membrane based on graphene quantum dots interlayer for enhanced gas separation performance

Thin Film Mixed Matrix Hollow Fiber Membrane Fabricated by Incorporation of Amine Functionalized Metal-Organic Framework for CO2/N2 Separation

Poly (Vinyl Alcohol) Composite Membrane with Polyamidoamine Dendrimers for Efficient Separation of CO2/H2 and CO2/N2

Amorphous Ni–B Alloy/ceramic Composite Membrane Prepared by an Improved Electroless Plating Technique

Preparation and Gas Separation of Amorphous Silicon Oxycarbide Membrane Supported on Silicon Nitride Membrane

Fabrication and Characterization of Poly(vinylidene Fluoride)–polytetrafluoroethylene Composite Membrane for CO2 Absorption in Gas–liquid Contacting Process

Molecular-level manipulation of polyamide membranes for high-performance H2/CO2 separation

Development of a P84/ZCC Composite Carbon Membrane for Gas Separation of H2/CO2 and H2/CH4