Preparation of continuous NH2–MIL-53 membrane on ammoniated polyvinylidene fluoride hollow fiber for efficient H2 purification

Wanbin Li,Pengcheng Su,Guoliang Zhang,Chong Shen,Qin Meng

DOI: https://doi.org/10.1016/j.memsci.2015.08.049

IF: 9.5

2015-01-01

Journal of Membrane Science

Abstract:A thin and continuous NH2–MIL-53 layer composed of Al(III) and 2-amino terephthalic acid has been successfully deposited on an ammoniated polyvinylidene fluoride (PVDF) hollow fiber under harsh synthetic conditions in N,N-dimethyl formamide (DMF) precursor solution at 423K. In order to enhance the solvent resistance and thermal stability of membrane, the hollow fiber was ammoniated by ethanediamine to become cross-linked. The amino groups formed on its surface provided high-density heterogeneous nucleation sites for strong adhesive growth of NH2–MIL-53. Results showed that the thin NH2–MIL-53 layer on ammoniated PVDF hollow fiber was inter-grown with thickness of only about 8μm. After activation by DMF at 423K for 5h and drying under vacuum at 423K for 12h, its permeance and ideal separation factor of H2/CO2 increased 330 and 5.46 times respectively. The prepared NH2–MIL-53/PVDF hollow fiber membrane exhibited excellent H2 permeance of 54.20×10−7mols−1m−2Pa−1 as well as the high ideal separation factor of 30.37, 24.07, 27.85 and 27.31 for H2/CO2, H2/O2, H2/N2 and H2/CH4, respectively. The composite membrane can also efficiently separate the H2/CO2 mixture with H2 permeance of 42.13×10−7mols−1m−2Pa−1 and separation factor of 32.35, which showed to be the highest separation factors among those reported for polymer supported MOF membranes.