Abstract:Nanosized copper oxide-zirconia particles containing 10-30 mol% of copper were prepared by using a precipitation technique in aqueous tetramethylammonium hydroxide solutions. Two methods, in situ (INS) and step-by-step (SBS), which differed in the time when the copper salt was introduced to the synthesis procedure, were used, and this allowed a comparison of the properties of the final powders produced using the two modes of preparation. The surface areas and phase compositions were different for the samples prepared from the two different methods after calcination at 500 degreesC. A surface area of 168 m(2) g(-1) was obtained for the sample prepared with the SBS method and 121 m(2) g(-1) for the INS method, both contain 30 mol% copper. Tetragonal ZrO2 was observed from X-ray diffraction patterns for all samples prepared with the SBS method, however, no separate phase of copper or copper oxide was observed. It is proposed that all of the copper is finely distributed on the surface of the ZrO2 particles with the SBS method. For the samples prepared from the INS method, tetragonal ZrO2 was obtained at a low copper content and the peaks indexed to tetragonal ZrO2 shifted to higher angle with the increase of copper content, indicating copper ions being incorporated into the lattice. An amorphous compound was obtained at high copper content (30 mol%). The phase change with the calcination temperature was also investigated for the INS sample containing 30 mol% copper. The studies show that tetragonal ZrO2 and copper oxide were present after calcination at 400 degreesC, and tetragonal ZrO2 with a small amount of monoclinic ZrO2, as well as copper oxide, formed after calcination at 700 degreesC. However, after heating at 500 degreesC, amorphous compounds were obtained, suggesting that 500 degreesC could be a phase transition point. The incorporation of copper in the ZrO2 lattice resulted in a loss of order in the ZrO2 structure when calcined at 500 degreesC, with a further increase in the calcination temperature leading to the phase change.

Preparation and characterization of CuO–ZrO2 nanopowders

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Microstructure Characters of Cu/ZnO Catalyst Precipitated Inside Microchannel Reactor

Effect of dopant loading and calcination conditions on structural and optical properties of ZrO2 nanopowders doped with copper and yttrium

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Interaction of Copper Oxide with Zirconium Dioxide Stabilized with Yttrium Oxide

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Structural Evolution and Catalytic Properties of Nanostructured Cu/Zro2 Catalysts Prepared by Oxalate Gel-Coprecipitation Technique

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Synthesis of ZnO and CuO nanoparticles via Sol gel method and its characterization by using various technique

The dispersed states of copper species on CuO/ZrO2 catalysts and its influence on the catalytic performance

The Nature of Cu/ZrO2 Catalyst: Experimental and Theoretical Studies

Effect of Processing Conditions on Sonochemical Synthesis of Nanosized Copper Aluminate Powders.

Deposition time effect on copper oxide nano structures, an analysis study using chemical method

Solvent free fabrication and thermal tuning of copper oxide-zirconium dioxide nanocomposite for enhanced photocatalytic efficacy

Preparation and characterization of ultrafine particle CuO/ZrO2 catalysts II. Effect of calcination temperature on the morphology of the catalyst

Structure Characterization and Monolayer Dispersion Phenomenon of MgO-ZrO2 Prepared by Co-precipitation

Cubic phase stability, optical and magnetic properties of Cu-stabilized zirconia nanocrystals

CHARACTERIZATION OF PROPERTY AND STRUCTURE OF CuO/Ce0.5Zr0.5O2 CATALYSTS