Abstract:The preparation of monolithic silica aerogels via non-supercritical drying is realized by the following procedures: (1) formation of silica alcogels with perfect network structure by controlling two-step hydrolysis and condensation reaction rates of tetraethoxysilane; (2) improvement and reinforcement of network structure and strength of silica gels through exchanging the pore fluid with ethanol solvent thoroughly, immersing of gels in the ethanol solutions of tetraethyoxysilane and aging; (3) gradual drying under ethanol fluid whose surface tension is much lower than water under ambient pressure. The resulting aerogels were characterized by means of SEM, TEM, TG-DTA, XRD, and adsorption-desorption techniques. It is found that the aerogels, which are made up of uniform spherical nanoparticles with diameters of about 10 nm, are of coherent network structures. Furthermore, the aerogels are porous, and the porosity is as high as 91%. The diameter of the pore sizes is in the range of 10 similar to 30 nm, and the density of the aerogels is low (200 similar to 400 kg . m(-3)). The specific surface area of the aerogels can be as high as 625. 65 m(2) . g(-1). The appearance, microstructure, diameters of primary particles and pore size distributions of the aerogels are in concordance with those prepared by conventional supercritical drying. It is demonstrated that the quality of the resulting aerogels is affected by the preparation conditions adopted in the preparation process. In fact, by adjusting the proportions of the reaction systems, and controlling the adding amounts of acid and base during the two-step hydrolysis and condensation process, silica aerogels with required density, definite strength and ideal morphology can be produced.

Preparation of Porous Silica from Fly Ash: an Experimental Study

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

The preparation of silica white from fly ash and its characterization

Preparation of precipitated silica from desilicated solution of high-alumina fly ash by dissolution with alkali: experiment and principle of polymerization of silicic acid

Study on preparation and surface modification of precipitated silica obtained from fly ash

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

Synthesis of porous silica gel and study on the adsorption of cerium

Preparation and Characterization of Microscaled Silica Areogel Balls by Emulsion Method

PREPARATION OF SILICA AEROGELS BY SUPERCRITICAL DRYING TECHNIQUE

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Preparation of Precipitated Nano-silica from Acid Leaching Residue of Coal Ash by Carbonation Method

Preparation of Silica by Alkaline-Heating and Precipitation Method from Corn Straw Ash

SYNTHESIS OF MESOPOROUS ALUMINOSILICATE WITH FLY ASH

Synthesis and Surface Strengthening Modification of Silica Aerogel from Fly Ash

Experimental Research on Preparation of High Specific Surface Area SiO_2 from Fly Ash

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

Atmospheric Drying Preparation and Microstructure Characterization of Fly Ash Aerogel Thermal Insulation Material with Superhydrophobic

Ambient Pressure Preparation,Surface Structure and Adsorption Properties of Silica Aerogels

Preparation of Silica Flatting Agent with Large Pore Volume by Using a Micro-sieve Reactor

Study on Slica-alumina Separated in Reacted Product of Baked High-alumina Fly Ash

Preparing Mesoporous Silica Aerogels from Diatomite