Thickness-dependent ferroelectric and magnetic properties of BiFeO_3 films

Wang Zhi-Jun,Huang Feng-Zhen,Du Ying-Chao,Jin Ya-Ming,Zhu Jin-Song

2012-01-01

Abstract:Room temperature multiferroic BiFeO3 material has recently become the focus of research for its potential applications in multifunctional devices.It is meaningful to systematically investigate the thickness-dependent properties of BiFeO3 films since the polarization of ferroelectrics have been reported to be size-dependent and the special cycloidal spin structure with a period of 62 nm could bring about additional complexity to BiFeO3.BiFeO3 films with various thicknesses are prepared on Si substrates by metal organic decomposition method.The microstructure,ferroelectricity and magnetism of the films are investigated by X-ray diffraction,the piezoresponse force microscope,and superconducting quantum interference device,respectively.It is found that the polycrystalline films exhibit ferroelectric properties even with thickness as low as 30 nm.The grain size increases rapidly first with the film thickness increasing from 30 nm to 120 nm,and then increases slowly.Similarly,the ferroelectric domain size also increases with increasing film thickness,which implies the probable enhancement of the ferroelectric polarization.The single-domain state is predominant for the grains with size about 47-104 nm,while multi-domain state can be found for larger grains.Moreover,the ferroelectric domain can be switched by voltages applied through the probe of piezoresponse force microscope.The magnetism of BiFeO3 also shows thickness dependence.The saturation magnetization MS decreases abruptly with the film thickness increasing up to 120 nm,and then it decreases much slower,which could be attributed to the variation of surface-to-volume ratio.