Abstract:The iron matrix composites strengthened with submicron/nano-sized TiC particles dopping with different alloying elements (Mo, Ni) were prepared by melt-in-situ reaction and one-step integrated hot compaction. The results indicate that the incorporation of Mo and Ni through alloying treatment can refine ceramic particles, and thus lead to a significant improvement in the uniformity of the microstructure. The mismatch between the TiC and α-Fe is significantly reduced and the interface stability is enhanced. The yield strength of 1904 MPa and maximum compressive strength of 2605 MPa of TiC/Fe composite with the addition of 4 wt.% Mo are 28.3% and 23.9% higher than those without alloying elements, respectively. The yield strength of 2032 MPa and maximum compressive strength of 2815 MPa of TiC/Fe composite with the addition of 2 wt.% Ni are 36.9% and 33.9% higher than those without alloying elements, respectively. First-principles calculation results indicate that Mo atoms tend to accumulate at the interface, while Ni atoms can easily substitute Fe atoms, resulting in the formation of a FeNi solid solution. The primary strengthening mechanisms of TiC/Fe composites dopping Mo are the refinement strengthening of ceramic particles. The interface bond between Fe matrix and TiC particles is also strengthened. The addition of Ni primarily leads to solid solution strengthening and grain refinement. This TiC particle manipulating strategy within Fe melt can effectively optimize the corresponding interfacial bonding, lead to comprehensive improvement in property, and finally realize the expanding application at specific wear locations.

Comprehensive experimental design based on dispersion and characterization of TiC nano powder

Preparation and Characterization of Ti(C,N)-based Nano-Cermets

Dispersion of Nano-Tin Powder in Aqueous Media

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Effect of nano-TiC addition on sinterability and mechanical properties of TiC high temperature ceramics

Ultrasonic Dispersion of Nano Tic Powders Aided by Tween 80 Addition

Research on Preparation of Nanocrystalline TiC Powers

Controlling the sizes of in-situ TiC nanoparticles for high-performance TiC/Al–Cu nanocomposites

Preparation of CNT/Cu Nano Composite Powder with Uniform Dispersion and Strong Interface Bonding by SP Method

Reinforced Copper Matrix Composites with Highly Dispersed Nano Size TiC In-Situ Generated from the Carbon Polymer Dots

Effects of nano-TiCp on the microstructures and tensile properties of TiCp/Al–Cu composites

Optimizing the Microstructure and Mechanical Behaviors of In-Situ TiC-γ′/Ni Composites by Subsequent Thermal Treatment

EFFECT OF POWDER DISPERSING ON MECHANICAL PROPERTIES OF Ti(C,N)-BASED CERMET

Grain Refinement and Mechanical Properties of Cu-Cr-Zr Alloys with Different Nano-Sized TiCp Addition.

Investigation of Dispersion for Nano-Tio2 in the Aqueous Medium

In Situ Formation of Ti Matrix Composites Reinforced Nanometric TiC by Powder Metallurgy Technique

TiB2/TiC nano-composite powder fabricated via high energy milling

Dispersion and Rheological Property of the Concentrated TiC Suspension

Preparation of Iron-Based Composites Reinforced with Submicron/nano-Sized TiC Ceramic Particles by In-Situ Reaction in Melts and One-Step Integrated Hot Pressing Densification

Microstructural heredity and controlling of strengthening particles in Fe(TiC)p composites fabricated by in-situ reaction