Abstract:Hot deformation behavior of the extruded Mg-6Gd-3Y (GW63) and Mg-6Gd-3Y-1Ag (GW63-1Ag) alloys was assessed by shear punch testing (SPT) method in the temperature range of 623 K to 723 K and shear strain rate of 1.6 × 10−2 to 1.3 × 10−1 s−1. Microstructural examinations showed that Ag addition decreased the initial grain size from 10.1 to 2.9 µm. According to the hot deformation results, hyperbolic-sine exponents (n-values) of 3.39 and 2.54 were obtained for the Ag-free and Ag-containing alloys, respectively. The corresponding activation energies were found to be 321 and 178 kJ mol−1 for these alloys. Therefore, the controlling deformation mechanisms were defined as viscous glide of dislocation for the Mg-6Gd-3Y alloy and grain boundary sliding for Mg-6Gd-3Y-1Ag. Processing maps were developed based on the dynamic material model (DMM) to determine the flow instability domains during hot deformation. Accordingly, the optimum hot working conditions were found to be in the temperature range of 655 K to 723 K and shear strain rate of 3.3 × 10−2 to 1.3 × 10−1 s−1 for the GW63-1Ag alloy, whereas the safe deformation window for the GW63 alloy was narrowed down to a temperature range of 665 K to 705 K and shear strain rate of 7.2 × 10−2 to 1.3 × 10−1 s−1. The Ag-containing alloy exhibited flow instability regions only at low temperatures and high strain rates. On the other hand, the Ag-free alloy demonstrated other instability domains comprising the formation of mechanical twins and cracking. Electron back-scattered diffraction analysis was utilized to correlate the microstructural evolution of the alloys after shear deformation to the hot working parameters. Continuous dynamic recrystallization was suggested as the main mechanism for generation of the dynamically recrystallized grains during hot deformation of both alloys.

High Temperature Deformation and Microstructural Evolution of Mg–Gd–Y Alloys

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Ductility enhancement in Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy fabricated through extrusion and equal channel angular pressing (EX-ECAP)

High temperature deformation behavior of Mg-5wt.%Y binary alloy: Constitutive analysis and processing maps

Deformation mechanism of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy under high temperature and high strain rates

Research on microstructure and mechanical properties of hot extruded Mg-Gd-Y-Sm-Zr alloy at room and high temperatures

Microstructure Evolution and Deformation Behavior of Extruded Mg-5Al-0.6Sc Alloy during Room and Elevated Temperature Tension Revealed by Ex-Situ EBSD and VPSC

The high-temperature deformation and microstructural evolution mechanism of Mg-Gd-Y-Zn-Zr alloy formed by CMT arc additive forming

Effects of extrusion temperature on microstructure evolution and mechanical properties of heterogeneous Mg−Gd alloy laminates via accumulated extrusion bonding

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

Hot Deformation Behavior and Processing Map of Coarse-Grained Mg–Gd–Y–Nd–Zr Alloy

Unveiling the Microstructural Features during Compression of a High-Modulus Mg-15Gd-8Y-6Al-0.3Mn Alloy Reinforced by a Large Volume of Al2RE Phases

Effect of Ag Addition on the Hot Deformation, Constitutive Equations and Processing Maps of a Hot Extruded Mg-Gd-Y Alloy

Effect of Mn and Sc on Microstructures and Mechanical Properties of Mg-9Gd-4Y Alloy

Temperature Effect on Strain Hardening Behaviors of As‐Extruded Binary Magnesium Alloys

Microstructure evolution, texture and mechanical properties of a Mg–Gd–Y–Zn–Zr alloy fabricated by cyclic expansion extrusion with an asymmetrical extrusion cavity: The influence of passes and processing route