Controllable Synthesis of One-Dimensional Chinelike Superstructures of Homogeneous Bi100–xSbx Alloys Via a Template-Free Electrodeposition

Bo Zhou,Xing-Hua Li,Jun-Jie Zhu

DOI: https://doi.org/10.1021/cg0704955

IF: 4.01

2007-01-01

Crystal Growth & Design

Abstract:One-dimensional (ID) superstructures are attracting increasing interests because of their unique physical and chemical properties. In our work, ID chinelike superstructures of homogeneous Bi100-xSbx (x = 0-100) alloys were synthesized in aqueous solutions via a template-free electrochemical route at room temperature. The cyclic voltammetric analysis and the X-ray diffraction (XRD) study proved that Bi-III and Sb-III can be coreduced as a homogeneous solid solution; the Bi/Sb ratio in the alloy was greatly correlated to that in the aqueous solution, while also being affected by the deposition potential. The structures of the products were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), and selected area electron diffraction (SAED). These I D chinelike superstructures consisted of orderly aligned subcrystallites with only slight orientational distortion. The formation of these ID superstructures was affected mainly by the deposition potential, and as the deposition potential became less and less negative, the products changed gradually from fine dendrites to big ID chinelike superstructures. The orientational distortion in the structure, which is the reason for the chinelike pattern, might enhance the phonon scattering at subcrystallite boundaries and thus reduce the thermoconductivity, resulting in the improvement of the thermoelectric property.