Abstract:A LiFePO4/C composite was synthesized by a simple solid-state reaction method using glucose as reductive agent and carbon source and FePO4 as precursor, which was prepared by introduction of Na3PO4 as phosphorus source and pH regulator in order to pursue lower cost and environmental protection. The structure and morphology of FePO4 and LiFePO4/C were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Furthermore, electrochemical performance of LiFePO4/C was investigated by galvanostatic charge–discharge tests and cyclicvoltammogram (CV). The results indicate that FePO4 obtained has a small particle size and uniform particle distribution, which is demonstrated to be applicable as the iron source to synthesize LiFePO4/C. Prepared LiFePO4/C shows an excellent rate capability and cycle performance. At rates of 0.1 C, 0.2 C, 1 C and 2 C, the initial discharge capacities of 161, 158, 145 and 120 mAh/g were achieved, respectively and the discharge capacity is 154, 153, 140 and 116 mAh/g after 400 cycles. The employed method of preparing FePO4 by introduction of Na3PO4 has advantages such as low cost, safe raw material, environmental benign and recyclable products, which is suitable for industrial production.

LiFePO4 prepared by carbothermal reduction method

Synthesis of LiFePO<sub>4</sub>/C by Carbon Thermal Reduction Method and Its Electrochemical Properties

LiFePO<sub>4</sub>/C Cathode Materials Prepared by One-Step Fast Carbothermal Method Using Fe<sub>2</sub>O<sub>3</sub> as Raw Materials

High Density LiFePO4/C Synthesized by Controlled Crystallization and Microwave Carbon Thermal Reduction

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Synthesis and Characterization of LiFePO4 by a New Synthetic Route

The preparation and characterization of LiFe0.98Mn0.02PO4/C by spraydrying and low temperature reduction route

An Improved Method to Prepare FePO4 by Introduction of Na3PO4 and Its Usage for Fabricating LiFePO4

Preparation and properties of LiFePO4/C composite materials with Fe2O3 as starting reactant

Morphology and Reaction Mechanism of LiFePO4 Prepared by Hydrothermal Synthesis

The preparation and characterization of LiFe0.98Ni0.01Nb0.01PO4/c by carbon reduction route

Modified Carbothermal Synthesis and Electrochemical Performance of LiFePO 4 /C Composite As Cathode Materials for Lithium-Ion Batteries

Low-cost, One-Step Process for Synthesis of Carbon-Coated LiFePO4 Cathode

LiFePO4 Cathode Materials with Enhanced Performance Prepared by a Novel Solid-State Method

Improving the rate and low-temperature performance of LiFePO4 by tailoring the form of carbon coating from amorphous to graphene-like

Enhanced Electrochemical Performance of LiFePO 4 /C Prepared by Sol–gel Synthesis with Dry Ball-Milling

Synthesis of LiFePO 4 -C Cathode Materials Using a Green and Low-Cost Method

Synthesis and electrochemical properties of LiFePO4/C composite cathode materials

Improving the Rate and Low-Temperature Performance of LiFePO 4 by Tailoring the Form of Carbon Coating from Amorphous to Graphene-Like

Preparation and Characterization of LiFePO4 Made from NH4FePO4·H2O

Facile synthesize LiFePO4 nanocomposites with excellent electrochemical properties as cathodes for lithium ion batteries