An Improved Method to Prepare FePO4 by Introduction of Na3PO4 and Its Usage for Fabricating LiFePO4

Xiurong Si,Min Li,Xu Fu

DOI: https://doi.org/10.1007/s11595-019-2165-0

2019-10-01

Abstract:<p class="a-plus-plus">A LiFePO<sub class="a-plus-plus">4</sub>/C composite was synthesized by a simple solid-state reaction method using glucose as reductive agent and carbon source and FePO<sub class="a-plus-plus">4</sub> as precursor, which was prepared by introduction of Na<sub class="a-plus-plus">3</sub>PO<sub class="a-plus-plus">4</sub> as phosphorus source and pH regulator in order to pursue lower cost and environmental protection. The structure and morphology of FePO<sub class="a-plus-plus">4</sub> and LiFePO<sub class="a-plus-plus">4</sub>/C were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Furthermore, electrochemical performance of LiFePO<sub class="a-plus-plus">4</sub>/C was investigated by galvanostatic charge–discharge tests and cyclicvoltammogram (CV). The results indicate that FePO<sub class="a-plus-plus">4</sub> obtained has a small particle size and uniform particle distribution, which is demonstrated to be applicable as the iron source to synthesize LiFePO<sub class="a-plus-plus">4</sub>/C. Prepared LiFePO<sub class="a-plus-plus">4</sub>/C shows an excellent rate capability and cycle performance. At rates of 0.1 C, 0.2 C, 1 C and 2 C, the initial discharge capacities of 161, 158, 145 and 120 mAh/g were achieved, respectively and the discharge capacity is 154, 153, 140 and 116 mAh/g after 400 cycles. The employed method of preparing FePO<sub class="a-plus-plus">4</sub> by introduction of Na<sub class="a-plus-plus">3</sub>PO<sub class="a-plus-plus">4</sub> has advantages such as low cost, safe raw material, environmental benign and recyclable products, which is suitable for industrial production.</p>

English Else