Abstract:A joint chemical reactor system referred to as an ultrasonic-intensified micro-impinging jetting reactor (UIJR), which possesses the feature of fast micro-mixing, was proposed and has been employed for rapid preparation of FePO4 particles that are amalgamated by nanoscale primary crystals. As one of the important precursors for the fabrication of lithium iron phosphate cathode, the properties of FePO4 nano particles significantly affect the performance of the lithium iron phosphate cathode. Thus, the effects of joint use of impinging stream and ultrasonic irradiation on the formation of mesoporous structure of FePO4 nano precursor particles and the electrochemical properties of amalgamated LiFePO4/C have been investigated. Additionally, the effects of the reactant concentration (C=0.5, 1.0 and 1.5molL−1), and volumetric flow rate (V=17.15, 51.44, and 85.74mLmin−1) on synthesis of FePO4·2H2O nucleus have been studied when the impinging jetting reactor (IJR) and UIJR are to operate in nonsubmerged mode. It was affirmed from the experiments that the FePO4 nano precursor particles prepared using UIJR have well-formed mesoporous structures with the primary crystal size of 44.6nm, an average pore size of 15.2nm, and a specific surface area of 134.54m2g−1 when the reactant concentration and volumetric flow rate are 1.0molL−1 and 85.74mLmin−1 respectively. The amalgamated LiFePO4/C composites can deliver good electrochemical performance with discharge capacities of 156.7mAhg−1 at 0.1C, and exhibit 138.0mAhg−1 after 100 cycles at 0.5C, which is 95.3% of the initial discharge capacity.

Morphology and Reaction Mechanism of LiFePO4 Prepared by Hydrothermal Synthesis

Rapid Preparation of High Electrochemical Performance LiFePO4/C Composite Cathode Material with an Ultrasonic-Intensified Micro-Impinging Jetting Reactor

Controllable Synthesis and Morphology Evolution of Hierarchical LiFePO4 Cathode Materials for Li-ion Batteries

Preparation of LiFePO4 Nanoparticles in Virtue of Triblock Copolymer P123 and Their Application in Li-ion Battery

Study on the Preparation of Lifepo4 by Hydrothermal Method

Synthesis and Characterization of LiFePO4 by a New Synthetic Route

Olivine LiFePO4 Nanocrystallites Embedded in Carbon-Coating Matrix for High Power Li-ion Batteries

Synthesises, Characterizations and Electrochemical Properties of Spherical-Like LiFePO4 by Hydrothermal Method

Preparation of Nano-spherical Iron Phosphate by Hydrothermal Method and Its Application as the Precursor of Lithium Iron Phosphate

Preparation and Characterization of LiFePO4 Made from NH4FePO4·H2O

Preparation and characterization of LiFePO4 made from NH4FePO4 center dot H2O

SYNTHESIS AND CHARACTERIZATION OF <font>LiFePO</font><sub>4</sub>/<font>C</font> PREPARED VIA A SOL–GEL METHOD

Preparation and Electrochemical Performance of Spherical LiFePO4

Effect of Particle Size of Li3PO4 on LiFePO4 Cathode Material Properties Prepared by Hydrothermal Method

Preparation of Precursor FePO4 and Its Effects on Electrochemical Properties of LiFePO4

Preparation and Characterization of LiFePO[sub 4] from a Novel Precursor of NH[sub 4]fepo[sub 4]⋅h[sub 2]O

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Synthesis of nano FePO 4 and electrochemical characterization of composite cathode material LiFePO 4/C

Preparation of lithium iron phosphate with superior electrochemical performances from titanium white by-product ferrous sulfate

Preparation and Performance of FePO_4 Precursor for LiFePO_4

LiFePO4 prepared by carbothermal reduction method