Abstract:Background: Conventional methods of preparing magnetoliposomes are complicated and inefficient. A novel approach for magnetoliposomes preparation was investigated in the study reported here.Methods: FeCl3/FeCl2 solutions were hydrated with lipid films to obtain liposome-encapsulated iron ions by ultrasonic dispersion. Non-encapsulated iron ions were removed by dialysis. NH3 center dot H2O was added to the system to adjust the pH to a critical value. Four different systems were prepared. Each was incubated at a different temperature for a different length of time to facilitate the permeation of NH3 center dot H2O into the inner phase of the liposomes and the in situ formation of magnetic iron-oxide cores in the liposomes. Single-factor analysis and orthogonal-design experiments were applied to determinate the effects of alkalization pH, temperature, duration, and initial Fe concentration on encapsulation efficiency and drug loading.Results: The magnetoliposomes prepared by in situ precipitation had an average particle size of 168+/-14 nm, zeta potential of -26.2+/-1.9 mV and polydispersity index of 0.23+/-0.06. The iron-oxide cores were confirmed as Fe3O4 by X-ray diffraction and demonstrated a superparamagnetic response. Encapsulation efficiency ranged from 3% to 22%, while drug loading ranged from 0.2 to 1.58 mol Fe/mol lipid. The optimal conditions for in situ precipitation were found to be an alkalization pH of 12, temperature of 60 degrees C, time of 60 minutes, and initial Fe concentration of 100 mM Fe3+ + 50 mM Fe2+.Conclusion: In situ precipitation could be a simple and efficient approach for the preparation of iron-oxide magnetoliposomes.

The synthesis and characterization of Magnetic Iron Oxide with high saturation magnetization

Synthesis and Characterisation of Transition Metal Iron Oxide Nanocomposite Crystals and Particles Using Wet Chemical Coprecipitation Method

Studies on the magnetic polymer with nanometer magnetic dispersing phase. (3). Studies on preparation and properties of Crx Fe3-xO4 nanocrystalline magnetic carrier

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Systematic Study on the Synthesis and Magnetism Properties of Manganese Ferrite MnFe2O4 by an Oxidation Roasting Process

Synthesis and characterization of magnetite nanoparticles by a simple solvothermal method

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Ion-Doped Iron-Based nanoparticles with enhanced magnetic properties: Synthesis and formation mechanism via coprecipitation

In Situ Precipitation: a Novel Approach for Preparation of Iron-Oxide Magnetoliposomes.

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Stabilized Bare Superparamagnetic Iron Oxide Nanoparticles: Synthesis and Characterization

Synthesis and characterization of nano-sized magnetic ferroferric oxide particles

Preparation and characterization of water-soluble monodisperse magnetic iron oxide nanoparticles via surface double-exchange with DMSA

Controlled Synthesis of Magnetic Iron Oxide Nanoparticles: Magnetite or Maghemite?

A More Efficient Pathway for Synthesis of Zinc-Doped Superparamagnetic Iron Oxide Nanocrystals with Enhanced Saturation Magnetization

Characterization of the Oxidation of Magnetite Nanoparticles during Their Synthesis by Different Structural Analysis Techniques

Synthesis of Nearly Monodisperse Iron Oxide and Oxyhydroxide Nanocrystals