Abstract:Iron oxide nanoparticles can be obtained through different methods and have been widely investigated for its potential use in different applications. In this work magnetite nanoparticles were synthesized using chemical co-precipitation at room temperature. NaOH and NH4OH were used as precipitating agents under nitrogen atmosphere and by applying vigorous stirring. Structural and physical characterization was achieved by using Transmission electron microscopy, X-ray diffraction and Dinamic light scattering. Our results showed differences in size and morphology, depending on the precipitating agent. The NaOH-magnetite nanoparticles showed a mixture of cubic-spherical morphology meanwhile the NH4OH-magnetite nanoparticles were mainly aspheric. Results from X-ray diffraction presented magnetite diffraction pattern when compare to the standard PDF 89-0691. Lattice parameter for NaOH-magnetite and NH4OH-magnetite was 0.8371 nm that is less than the reported of 0.8396 nm. This could be an indicator of oxidation of the crystal surface and formation of the maghemite phase when the nanoparticles were exposed to air. The average size of the nanocrystals was 13 nm for NaOH-magnetite and NH4OH-magnetite. From Dynamic light scattering experiments the NaOH-magnetite nanoparticles presented an average Z diameter larger than NH 4OH-magnetite (253 nm vs 152 nm); this may be to a less stability in water, which provoked a higher aggregation degree. Polydispersity Index for NaOH-magnetite was 0.445 and for NH4 OH-magnetite was 0.397. According to the International Organisation for Standardisation NaOH-magnetite nanoparticles were widely polydisperse whereas NH4OH-magnetite nanoparticles were moderately polydisperse. Our results showed that the chemical co-precipitation method at room temperature can achieve good quality and synthesized nanoparticles similar to those obtained by other more complex techniques.

Characterization of the Oxidation of Magnetite Nanoparticles during Their Synthesis by Different Structural Analysis Techniques

Synthesis and Characterisation of Transition Metal Iron Oxide Nanocomposite Crystals and Particles Using Wet Chemical Coprecipitation Method

Synthesis And Characterization Of Uniform And Crystalline Magnetite Nanoparticles Via Oxidation-Precipitation And Modified Co-Precipitation Methods

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

Controlled Synthesis of Magnetic Iron Oxide Nanoparticles: Magnetite or Maghemite?

Synthesis And Characterization Of Superparamagnetic Maghemite Nanoparticles

Preparation, phase analysis and electrochemistry of magnetite (Fe3O4) and maghemite (γ-Fe2O3) nanoparticles

SYNTHESIS AND CHARACTERIZATION OF MAGNETITE BY THE COPRECIPITATION METHOD AT ROOM TEMPERATURE

Synthesis And Characterization Of Magnetite Particles By Co-Precipitation Method

Monodisperse magnetite nanoparticles synthesis and their thermal-stability

Preparation And Characterization Of Magnetite Nanoparticles With Various Morphologies By One Method

Synthesis and Characterisation of Iron Oxide Nanoparticles with Tunable Sizes by Hydrothermal Method

Preparation and characterization of magnetite Fe3O4 nanopowders

Energetic Electron-Assisted Synthesis of Tailored Magnetite (Fe3O4) and Maghemite (γ−Fe2O3) Nanoparticles: Structure and Magnetic Properties

The Synthesis of Octahedral Nanoparticles of Magnetite

The synthesis and characterization of Magnetic Iron Oxide with high saturation magnetization

Synthesis, characterization, and dielectric studies of magnetic iron oxide nanoparticles

Synthesis And The Characteristics Of Iron/Iron Oxide Nanoparticles

A New Nonhydrolytic Synthesis of Magnetite Nanocrystallites in the Presence of Ω‐functionalized Polystyrene Matrix

Preparation and Magnetic Properties of Magnetite Nanoparticles by Sol–gel Method

Synthesis of Nanometer-Size Maghemite Particles from Magnetite