Abstract:As-cast Mg97Y2Zn1 billets with a two-phase microstructure were processed with four passes of equal channel angular extrusion (ECAE) using different routes (A, B-c and C) at 350 degrees C to refine the microstructure. The duplex microstructure of this material consists of a Mg-rich alloy matrix with a long-periodic-stacking-order (IPSO) reinforcement phase. Mechanical properties were evaluated under both quasi-static and dynamic loading conditions. It was found that routes A and B-c were more effective in producing a Mg alloy with nearly isotropic properties. For route C, the specimens more easily fractured due to pre-existing localized shear planes induced by ECAE. Microstructural observations revealed that the post-processed average matrix grain size could be as fine as similar to 1 mu m. Uniaxial compressive loading and micro-hardness measurements verified the enhancement of strength, and it was noticed that the increase of strength comes primarily from grain refinement of the Mg matrix. In the composite, we also focused on elucidating the deformation mechanism of the LPSO phase. It is believed that localized deformation is responsible for the final failure of the ECAE processed Mg97Y2Zn1 alloy under both quasi-static and high strain rate loading. The grain morphology and distribution after deformation indicated that the shear localization resulted from the rotation and rearrangement of grains. Moreover, cracks were found to propagate along the grain boundaries leading to final failure.

Effect of Solution Treatment on Microstructure Evolution and Mechanical Properties of Mg-6.0Zn-0.6Y-0.5Zr Alloy Processed by Equal Channel Angular Extrusion

Effect of ECAE Conditions on the Microstructure, Texture and Mechanical Properties of an Extruded Mg–Zn–Y–Zr Alloy

Influence of Pre‐Solution Treatment on Microstructure and Mechanical Properties of Mg–Gd–Nd–Zn–Zr Alloy Processed by ECAP

Preparing Mg-6Al alloy with high mechanical properties and fine grains by equal channel angular extrusion

Effect of Equal Channel Angular Extrusion on the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

A Study of Microstructure Evolution for Mg Alloy Subjecting to Multi-Pass Equal Channel Angular Extrusion

Effects of ECAE Temperature and Billet Orientation on the Microstructure, Texture Evolution and Mechanical Properties of a Mg–Zn–Y–Zr Alloy

Influence of Equal Channel Angular Extrusion on the Properties of Mg-6Al Alloy

Microstructure Evolution of Processed Mg-Al-Zn Alloy by Equal Channel Angular Extrusion in Semi-Solid Isothermal Treatment

Precipitation behaviors and mechanical properties of a solution-treated Mg-Gd-Nd-Zn-Zr alloy during equal-channel angular pressing process

Microstructure and mechanical properties of AZ31 Mg alloy processed by two-step equal channel angular extrusion

The Microstructure and Mechanical Properties of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion

Effect Of Solution Treatment And Extrusion On The Microstructure And Mechanical Properties Of A Mg-2gd-Nd-0.4zn-0.3zr Alloy

Microstructure Evolution and Mechanical Properties of AZ 31 Mg Alloy Processed by Equal Channel Angular Extrusion

Microstructure Evolution and Mechanical Behavior of Mg-10Gd-3Y-0.4Zr Alloy Processed by ECAP at High Temperature

Microstructural Evolution and Mechanical Properties of Mg95.5Y3Zn1.5 Alloy Processed by Extrusion and ECAP

Microstructure Evolution and Mechanical Properties of AZ80 Mg Alloy during Annular Channel Angular Extrusion Process and Heat Treatment

Mechanical Properties and Failure of ECAE Processed Mg97Y2Zn1 at Different Strain Rates

Effect of equal channel angular extrusion process on deformation behaviors of Mg-3Al-Zn alloy

Microstructure and Tensile Properties of Magnesium Alloy Containing Quasicrystallines Processed by Equal-Channel-Angular-Extrusion

Mechanical Properties and Microstructure of AZ31 Mg Alloy Processed by Two-Step Equal Channel Angular Extrusion