Abstract:Development of cost-effective repair and rejuvenation processes for Directionally Solidified (DS) Ni-based superalloy blades are of great economic and technological meanings. Laser deposition is a promising rejuvenation candidate for DS blades due to its precise controllability on heat input, solidification conditions, deposition geometry and microstructure. However, one of the challenges for rejuvenating DS blade is the extremely high liquation and cracking susceptibility. Boundary liquation and interface cracking frequently occur during laser deposition on the DS Ni-based superalloy blade. It is not clear the real mechanism of liquation happened in DS blade during laser deposition, to clarify the liquation mechanism on DS blade is then vital for developing a practical laser deposition technology for crack-free rejuvenation.Based on systematic experimental results and analyses on laser deposition on DS Ni-based substrate, this paper exhibits the boundary liquation and interface cracking phenomena, and approves that the liquation during laser deposition on DS substrate originates from the melting of the periphery of small WC carbides in grain boundary in the heat affected zone, instead of the as-believed melting of eutectics in the grain boundary. The melting of the carbide periphery further develops, connects with each other, propagates along the grain boundary and finally forms a liquid film and then the cracking. Based on this understanding, two approaches were then proposed to achieve crack-free laser deposition rejuvenation for DS superalloy blades.

Boundary Liquation and Interface Cracking Characterization in Laser Deposition of Inconel 738 on Directionally Solidified Ni-based Superalloy

Cracking Mechanism and Susceptibility of Laser Melting Deposited Inconel 738 Superalloy

Direct laser deposition of Inconel 738 on directionally solidified Ni-base supperalloy component

Liquation Mechanism Analysis on Laser Deposition on Directionally Solidified Superalloy Blade for Crack-Free Rejuvenation

A Study on the Cracking Behaviour in Laser Metal Deposition of IC10 Directionally Solidified Nickel-Based Superalloy

Characterization of Heat Affected Zone Liquation Cracking in Laser Additive Manufacturing of Inconel 718

Influences of Cooling Conditions on the Liquation Cracking in Laser Metal Deposition of a Directionally Solidified Superalloy

Origin of hot cracking formation and suppression method in laser additive manufactured nickel-based superalloys

Inhibition of Cracking by Grain Boundary Modification in a Non-Weldable Nickel-Based Superalloy Processed by Laser Powder Bed Fusion

Crack Inhibition of Non-Weldable Inconel 738 Alloy in Ultrasound-Assisted Laser Directed Energy Deposition

Investigation of Dendritic Growth and Liquation Cracking in Laser Melting Deposited Inconel 718 at Different Laser Input Angles

Investigating crack formation in IN738LC Ni-based superalloy fabricated by laser powder-bed fusion process

Investigation on the hot crack sensitivity of a nickel-based single crystal superalloy fabricated by epitaxial laser metal forming

Dendritic Microstructure and Hot Cracking of Laser Additive Manufactured Inconel 718 under Improved Base Cooling

Design of a novel crack-free precipitation-strengthened nickel-based superalloy and composites for laser powder bed fusion

Hot cracking behavior and mechanism of the IC10 directionally solidified superalloy during laser re-melting

Liquefaction Characteristics and Cracking Behavior of the Grain Boundaries and Interdendritic Regions in Non-Weldable K447A Superalloy During Laser Re-Melting

Liquation Cracking in Fiber Laser Welded Joints of Inconel 617

Laser cladding repairing of directionally solidified nickel base superalloy and its tensile properties

Avoiding Cracks in Additively Manufactured Non-Weldable Directionally Solidified Ni-based Superalloys

Mechanical Performance of Laser Deposition Repairing of in 738 on Directionally Solidified Superalloy Blade