Abstract:The purpose of this study was to evaluate the feasibility of repairing defective turbine blades made of Inconel 738 using additive manufacturing called laser metal deposition with the use of Inconel 718 powder. The deposition process was conducted on substrates using varying laser power, 150, 250 and 350 (W). The experimental results indicate that as the laser power is raised, there is a corresponding increase in the average of substrate melting depth, 33.42–405.12 (μm), the average of interface thickness, 2.85–10.20 (μm) and the amount of dilution, 0.036–0.684 (%). The substrate's volume percentage and the average size of the γ' phase exhibit larger values prior to the deposition procedure compared to the subsequent stages. The augmentation of laser power resulted in a proportional rise in both the volume percentage and average size of the γ' phase within the substrates. At the location near the interface of the first layer, graining is preferentially in the direction of heat transfer and crystal growth. A narrow unmixed zone was formed along the melting line in the substrate and first layer's interface, that whit increased laser power, area of this zone decreased, 7.27 to almost 0 (μm). As the layers approach the surface, the grains become unidirectional and coaxial growth. Increasing the laser power increased the average grain size of the layers. Le but de cette étude était d'évaluer la faisabilité de réparer des aubes de turbine défectueuses en Inconel 738 à l'aide de la fabrication additive qu'on appelle dépôt de métal par laser en utilisant la poudre d'Inconel 718. On a réalisé le procédé de dépôt sur des substrats en utilisant des puissances de laser variées, 150, 250 et 350 (W). Les résultats expérimentaux indiquent qu'à mesure que la puissance du laser augmente, il y a une augmentation correspondante de la profondeur moyenne de fusion du substrat, de 33.42 à 405.12 (μm), de l'épaisseur moyenne de l'interface, de 2.85 à 10.20 (μm) et de la quantité de dilution, de 0.036 à 0.684 (%). Le pourcentage volumique du substrat et la taille moyenne de la phase γ' montrent des valeurs plus élevées avant la procédure de dépôt par rapport aux étapes subséquentes. L'augmentation de la puissance du laser a abouti à une augmentation proportionnelle du pourcentage volumique et de la taille moyenne de la phase γ' dans les substrats. À l'endroit près de l'interface de la première couche, le grainage s'effectue préférentiellement dans la direction du transfert de chaleur et de la croissance cristalline. Une zone étroite non mélangée s'est formée le long de la ligne de fusion à l'interface du substrat et de la première couche, laquelle avec la puissance accrue du laser, a diminué de 7.27 à presque 0 (μm). À mesure que les couches se rapprochent de la surface, les grains deviennent unidirectionnels avec croissance coaxiale. L'augmentation de la puissance du laser a augmenté la taille moyenne de grain des couches.

Direct Laser Deposition of Inconel 738 on Directionally Solidified Ni-base Superalloy Component

Mechanical Performance of Laser Deposition Repairing of in 738 on Directionally Solidified Superalloy Blade

Boundary Liquation and Interface Cracking Characterization in Laser Deposition of Inconel 738 on Directionally Solidified Ni-based Superalloy

Liquation Mechanism Analysis on Laser Deposition on Directionally Solidified Superalloy Blade for Crack-Free Rejuvenation

Effect of thermal cycles on laser direct energy deposition repair performance of nickel-based superalloy: Microstructure and tensile properties

Laser Preheating for Hot Crack Reduction in Direct Metal Deposition of Inconel 738LC

A novel method to prevent cracking in directed energy deposition of Inconel 738 by in-situ doping Inconel 718

Laser cladding repairing of directionally solidified nickel base superalloy and its tensile properties

The Effect of Optimized Substrate Orientation on Layer Step in Laser Metal Deposition of Single-Crystal Nickel-Base Superalloys

Influence of processing parameters on the thermal history, microstructure and tensile properties of Inconel 738 produced by laser directed energy deposition

Investigating laser power in AM-LMD process on the Inconel 718 powder deposited profile microstructure, aiming to repair gas turbine blades

Deposition of Nickel-Based Superalloy Claddings on Low Alloy Structural Steel by Direct Laser Deposition

A Study on the Cracking Behaviour in Laser Metal Deposition of IC10 Directionally Solidified Nickel-Based Superalloy

Influence of pulsed laser scanning patterns on microstructural evolution and mechanical properties of Inconel 718 in direct laser deposition

Laser Engineered Net Shaping of Nickel-Based Superalloy Inconel 718 Powders onto AISI 4140 Alloy Steel Substrates: Interface Bond and Fracture Failure Mechanism

Influence of post-heat treatments on the microstructure and mechanical properties of Inconel 738 produced by laser directed energy deposition

The effect of interval pulsed laser deposition on the microstructure and mechanical properties of Inconel 718 parts using laser directed energy deposition

Enhanced wear resistance of Ti reinforced Inconel 718 superalloy manufactured by laser directed energy deposition

Crack initiation and propagation within nickel-based high-temperature alloys during laser-based directed energy deposition: A review

Effect of deposition strategy and post processing on microstructure and mechanical properties of serviced Inconel 625 parts repaired using laser directed energy deposition

On the control of epitaxial growth and stray grains during laser-directed energy deposited Ni-based single crystal superalloy