Abstract:Improving the thickness of superconducting layer in coated conductors is an effective way to enhance its critical current. In this work, tri-layer YBCO/YBCO/YDyBCO films were successfully deposited on buffered Hastelloy substrate using the multi-coating lowfluorine metal-organic decomposition (LF-MOD) method and the thickness of the films can be up to 2.4 mu m. The effects of high-temperature annealing time on microstructures and superconducting properties of the films were systematically studied. Energy dispersive X-ray spectroscopy (EDS) results reveal that there remains a large amount of F element in the upper layer of the film when the annealing time is too short. With increasing the annealing time, the fluoride-containing precursor converts to YBCO grains completely. But the coarsening of grains appeared, and the critical current density (J (c)) of the film dropped slightly when the annealing time is too long. The cross-sectional scanning electron microscope (SEM) image and EDS plane analysis were applied to investigate the microstructure and element distribution of the final triple-layer YBCO films, respectively. The critical current of the final YBCO superconducting film could reach 316 A (77 k, self-field) for 1.2-cm-wide tapes with the optimal annealing conditions.

Fabrication and Interface Reaction of Y-Ba-Cu-O Superconducting Thin-Films by Reactive Ion-Beam Coating

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Insitu Fabrication Of Ybco/Ysz/Si Thin-Films By Laser Ablation

Enhancing superconductivity of ultrathin YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> films by capping non-superconducting oxides*

Fabrication And Analysis Of Tri-Layer Yba2cu3 O (7-Delta) Thick Films By Low-Fluorine Mod Method

Enhancing Superconductivity of Ultrathin YBa2Cu3O7-δ Films by Capping Non-Superconducting Oxides*

Thick REBaCuO Superconducting Films Through Single-Coating of Low-Fluorine Metallorganic Solution

Studies of high temperature superconducting thin films by transmission electron microscopy

Ion Beam Structure Modification of YBa2Cu3O7−x Coated Conductors Prepared by Solution Techniques

STUDY OF THE PREPARATION OF HIGH Tc SUPERCONDUCTING YBCO THIN FILMS BY A PLASMA-ASSISTED MOCVD PROCESS

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

Fabrication and Analysis of Tri-layer YBa2Cu3O7−δ Thick Films by Low-Fluorine MOD Method

Superconducting properties and structural perfection of epitaxial YBa 2 Cu 3 O 7- x thin films

HIGH Tc SUPERCONDUCTING THIN FILMS BY CHEMICAL SPRAY DEPOSITION

Fabrication of Superconducting YBa2Cu4O8 Film via Coprecipitation

Microstructural characterization of YBa2Cu3O7-x thin films grown on Y-ZrO2

Effects of BaCO3 in transient liquid-assisted fluorine-free metal organic deposition on the growth process of YBCO

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>

A New Method to Obtain Cu Films with Lower Resistivity and Higher Interface Adhesion on Different Substrates

THE COATED SUPERCONDUCTOR FILM OF YBa2Cu3O7-δ PREPARED BY COLLOIDAL PROCESSING

Co-deposition growth and superconductivity of La 2 − x Sr x Cu O 4 films by reactive molecular beam epitaxy