Preparation of HEMA gel-casted SiC ceramics combined with LPS sintering
Zixuan Qin,Wentao Xu,Junrong Ling,Tinghai Mu,Youfu Zhou
DOI: https://doi.org/10.1016/j.ceramint.2020.12.151
IF: 5.532
2021-04-01
Ceramics International
Abstract:<p>Densified SiC ceramics were prepared by using gel-casting method combined with liquid-phase sintering (LPS). In this study, a low-toxicity gel-casting system based on 2-hydroxyethyl methacrylate (HEMA) and N, N′-methylene acrylamide (MBAM) as monomer and crosslinker respectively, was first applied to SiC fabrication. The effects of the processing parameters on gel-casting were investigated in detail to achieve optimized rheological behavior and green body strength. The best result was obtained in the slurry with solid content of 50 vol%, dispersant of 0.4 wt% and monomer/crosslinker ratio of 20 at pH10. With the modified ternary sintering aids (Al<sub>2</sub>O<sub>3</sub>–Y<sub>2</sub>O<sub>3</sub>–CeO<sub>2</sub>) added, the densification can be realized at low temperature. After pressureless sintering at 1850 °C for 2 h, the sample with best mechanical properties was obtained. The highest relative density, hardness, flexural strength and fracture toughness were 96.23%, 24.94 GPa, 423.95 MPa and 4.78 MPa/m<sup>1/2</sup>, respectively. Present work provides an environmentally friendly and energy-saving process for preparing SiC ceramics with excellent properties.</p>
materials science, ceramics