Abstract:Gelcasting is a new ceramic forming technology for making complex-shaped ceramic products with high performance. The processes used in gelcasting are similar to processes often used in conventional ceramic forming process. However, when new high performance materials are introduced with the aim to improve the strength, defects such as air bubbles or agglomerates that can be found in many traditional ceramic materials are no longer be allowed since this would reduce the performance and reliability of the final ceramic products. The aim of this thesis project was to find an appropriate recipe of the ceramic suspension meanwhile improving the process of gelcasting and obtaining ceramic products with excellent mechanical behavior. To achieve this specified target, alumina and zirconia powders were studied in the following experiments which included rheological measurement of viscosity and storage modulus measurement for ceramic suspensions and drying shrinkage measurement of cast materials. The binder was burned out and the density was measured for ceramic materials sintered at different temperatures. The mechanical strength of sintered materials with high density was evaluated and the microstructure of fracture surfaces of ceramic samples was studied. Through rheological measurement, a good balance between fluidity and solid content of ceramic suspension was found. For alumina suspensions a solid content of 55vol% was selected and for zirconia solid contents of 46, 48 and 50vol% were studied. A monomer was dissolved in the suspension and an initiator was added to facilitate the polymerization of the monomer when the temperature was increased to around 70oC. The failure analysis of the fractured bending bars showed that the defects that caused the failure were not air bubbles but agglomerates. As a result, in future research for ceramic gelcasting with the intention to improve the mechanical strength, the suggestion is to use an appropriate recipe for the ceramic suspension and focus on elimination of granules and agglomerates from the suspension

Alumina gelcasting by using HEMA system

A Synergistic Low‐Toxicity Gelcasting System by Using HEMA and PVP

Gelcasting of low-toxity HEMA system alumina improved with PVP

Gelcasting of Alumina Ceramic in Mixed PVP–HEMA Systems

Gelcasting of Alumina with a Mixed PVP–MAM System

Gelation Forming Process for Toxicity-Free or Low-Toxicity System

Gelcasting of Alumina Via Cross-Linking of a Polyelectrolyte Dispersant

Room-temperature Gelcasting of Alumina with Tartaric Acid and Glutaraldehyde

Gelcasting of Alumina Ceramic in Presence of Water-Soluble Polymer

Gelcasting of Alumina Ceramic Components in Nontoxic Na-alginate–CaIO3–PVP Systems

Gelcasting of alumina suspension using gellan gum as gelling agent

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

New gel-casting process for alumina ceramics based on gelation of alginate

Mechanical and Electrical Properties of Lithium Stabilized Sodium Beta Alumina Solid Electrolyte Shaping by Non-Aqueous Gelcasting

Gelcasting of ceramic suspension in acrylamide/polyethylene glycol systems

Alumina casting based on gelation of gelatine

Gel Casting of High Strength Ceramics

Dispersion and Gelation Properties of Alumina Systems with Isobam Assisted by Dicarboxylic Acids

Preparation of HEMA gel-casted SiC ceramics combined with LPS sintering

Fabrication of Alumina Green Body Through Gelcasting Process Using Alginate

Study On Gel-Tape Casting In The Mixed Polyvinyl Alcohol And Acrylamide Systems